采用水热法在低温下制备了MnxZn1-xS纳米线.MnxZn1-xS纳米线的形貌和微观结构用透射电子显微镜和X射线衍射仪进行表征.磁性能用振动样品磁强计进行测试.MnxZn1-xS的形貌取决于Mn的含量和在ZnS纳米粒子内外的分布.未掺杂Mn的ZnS纳米线的直径和长度分别为80～200nm和10～20μm.随着Mn含量的增加,MnxZn1-xS纳米线的平均直径逐渐增加,长径比不断减小.X射线衍射结果表明MnxZn1-xS纳米结构结晶性好,为六方纤锌矿结构.在Mn的掺杂量为0.25%时,矫顽力达到最大.随着Mn掺杂量的增加,饱和磁化强度也不断非线性增强.
MnxZn1-xS nanowires were synthesized by hydrothermal method at low temperature.The morphology and microstructure of ZnS nanowires doped with Mn element were characterized by TEM and XRD.And the magnetic properties of them were examined by VSM(Lakeshore).The morphologies of MnxZn1-xS depend on the content of Mn and the Mn 10～20 μm,respectively.With the increase of Mn content in the ZnS,the mean diameter of nanowires increased and the aspect ratio of nanowires decreased.The XRD patterns revealed that MnxZn1-xS nanostructures were crystallized well with hexagonal wurtzite structure.The intensity of coercive force attained its maximum at 0.25%Mn incorporation.Saturation magnetization increased with the increase of Mn concentration non-linearly.
参考文献
| [1] | Nalwa;Heimbrodt W;Klar P J.Magnetic Nanostructures[M].Stevenson Ranch:American Scientific Publishers,2002 |
| [2] | Biswas S;Kar S;Chaudhuri S .[J].Journal of Physical Chemistry B,2005,109:17526. |
| [3] | Brieler F J;Grundmann P;Fr(o)ba M et al.[J].Journal of the American Chemical Society,2004,126:797. |
| [4] | Pavle V Radovanovic;Carl J Barrelet;Silvija Gradecˇak .[J].Nano Letters,2005,5:1409. |
| [5] | Garlick G F J;Gibson A F .[J].Journal of the Optical Society of America,1949,39:935. |
| [6] | Tang W.;Cameron DC. .ELECTROLUMINESCENT ZINC SULPHIDE DEVICES PRODUCED BY SOL-GEL PROCESSING[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1996(1/2):221-226. |
| [7] | Mastio EA.;Cranton WM.;Thomas CB.;Fogarassy E. .Ablation study on pulsed KrF laser annealed electroluminescent ZnS : Mn/Y2O3 multilayers deposited on Si[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2000(0):35-39. |
| [8] | Sch(o)n S;Chaichimansour M;Park W et al.[J].Journal of Crystal Growth,1997,175-176:598. |
| [9] | Hideki Kina;Yoji Yamada;Yukihiro Maruta et al.[J].Journal of Crystal Growth,1996,169:33. |
| [10] | Kovtyukhova N I;Buzaneva E V;Waraksa C C et al.[J].Chemistry of Materials,2000,12:383. |
| [11] | Althues H;Palkovits R;Rumplecker A et al.[J].Chemistry of Materials,2006,18:1068. |
| [12] | Gan LM.;Chew CH.;Xu SJ.;Chua SJ.;Loy GL.;Xu GQ.;Liu B. .ENHANCED PHOTOLUMINESCENCE AND CHARACTERIZATION OF MN-DOPED ZNS NANOCRYSTALLITES SYNTHESIZED IN MICROEMULSION[J].Langmuir: The ACS Journal of Surfaces and Colloids,1997(24):6427-6431. |
| [13] | Kasper J S;Roberts B W .[J].Physical Review,1956,101(02):537. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%