模拟油田CO2驱油现场环境,利用高温高压反应釜,采用失重法、扫描电镜（SEM）、X射线衍射（XRD）等方法,研究了不同CO2分压对X80管线钢腐蚀性能的影响。结果表明,X80管线钢的腐蚀速率随着CO2分压的升高呈先升高后下降的趋势,在CO2分压为1.5MPa时达到最大值。当CO2分压为0 MPa和0.5 MPa时发生均匀腐蚀,当分压升高到1.5MPa和2MPa时发生了局部腐蚀。CO2分压为0MPa时的腐蚀产物为非晶态物质,其余各分压下的腐蚀产物均以FeCO3为主。随着CO2分压的升高,腐蚀产物与基体结合的紧密度随着CO2分压的升高越来越紧密;腐蚀产物膜厚度呈先升高后降低的趋势,与腐蚀速率的变化相对应。
The effect of CO2 partial pressure on corrosion resistance of X80 pipeline steel was investigated in high temperature and pressure autoclave simulating the downhole environment of an oil field,using the weight loss method,SEM and XRD.The results showed that with increasing CO2 partial pressure,the corrosion rate of X80 pipeline steel showed the tendency of fluctuation,and the maximum rate appeared at the CO2 partial pressure of 1.5 MPa.Uniform corrosion occurred when the CO2 partial pressure was 0 MPa and 0.5 MPa.When the CO2 partial pressure was 1.5 MPa and 2 MPa,localized corrosion occurred.The corrosion product was composed of noncrystalline substance at partial pressure of 0 MPa,and mainly composed of FeCO3 at other partial pressures.With increasing the CO2 partial pressure,the combination between corrosion product and substrate was increasingly close,and the thickness of corrosion product showed the tendency of fluctuation,corresponding to the change in corrosion rate.
参考文献
| [1] | 张伟卫 .高级别管线钢抗CO<,2>腐蚀机理及生产工艺研究[D].北京科技大学,2007. |
| [2] | J.L.Crolet;M.R.Bonis .How to pressurize autoclaves for corrosion testing under carbon dioxide and hydrogen sulfide pressure[J].Corrosion: The Journal of Science and Engineering,2000(2):167-182. |
| [3] | 陈东,柳伟,路民旭,吴荫顺,侯世颖,陈迎锋.CO2分压对N80钢腐蚀产物膜保护性能的影响[J].北京科技大学学报,2007(03):288-292. |
| [4] | 陈卓元,张学元,王凤平.二氧化碳腐蚀机理及影响因素[J].材料开发与应用,1998(05):34. |
| [5] | 周琦,贾建刚,南雪丽,臧树俊,赵红顺,程新兰.CO2环境介质下16Mn钢的高温高压腐蚀性能[J].兰州理工大学学报,2008(01):14-18. |
| [6] | 刘会,朱世东,赵国仙,吕祥鸿.动态和静态下CO2分压对P110钢腐蚀行为的影响[J].腐蚀与防护,2009(08):551-554. |
| [7] | 何庆龙,孟惠民,俞宏英,樊自拴,王旭东,孙冬柏.N80油套管钢CO2腐蚀的研究进展[J].中国腐蚀与防护学报,2007(03):186-192. |
| [8] | 冯蓓,杨敏,李秉风,王栋.二氧化碳腐蚀机理及影响因素[J].辽宁化工,2010(09):976-979. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%