Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip, the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh water and 3.5% NaCl solution were measured experimentally,and the PH and electrode potential within crack were also measured continuously along with crack propagating.It showed that the increase of crack growth rate,caused by both decreasing frequency and raising stress ratio,was mainly accelerated by hydrogen embrittlement.