设计了3种方案对新型α型Ti-6Ta合金板材进行封头冲压成形试验,在冲压的封头不同部位取样进行压扁、拉伸、硬度、金相等相关检测和分析.结果表明:Ti-6Ta合金封头不适合采用冷冲压成形法成形;在Ti-6Ta合金板材表面涂敷高温防氧化涂层,采用315 t四柱油压机,在680 ～ 700℃温度下进行热冲压成形,能够得到表面质量良好的规格为φ219 mm×7.42 mm的Ti-6Ta合金封头;封头的组织形貌与原始板材相比无明显变化,其压扁工艺性能合格,强度及硬度与母材基本相当,可以满足Ti-6Ta合金承压设备的制造要求.
参考文献
| [1] | Roderick Hyde;Muriel Ishikawa;Nathan Myhrvold;John Nuckolls;Lowell Wood.Nuclear fission power for 21st century needs: Enabling technologies for large-scale, low-risk, affordable nuclear electricity[J].Progress in nuclear engergy,20082/6(2/6):82-91. |
| [2] | P.K. Dey;N.K. Bansal.Spent fuel reprocessing: A vital link in Indian nuclear power program[J].Nuclear engineering and design,20067/8(7/8):723-729. |
| [3] | Baldev Raj;U. Kamachi Mudali.Materials development and corrosion problems in nuclear fuel reprocessing plants[J].Progress in Nuclear Energy,20064(4):283-313. |
| [4] | Karen Alves de Souza;Alain Robin.Preparation and characterization of TI-Ta alloys for application in corrosive media[J].Materials Letters,200320(20):3010-3016. |
| [5] | 徐潇潇;崔岚;邱绍宇;李思凡;盛钟琦;邰江.Ti-5%Ta钛合金在乏燃料模拟溶解液中的腐蚀行为[J].核动力工程,2005(4):406-409. |
| [6] | 吴金平,杨英丽,赵恒章,赵彬,奚正平.焊接热循环对Ti35钛合金组织性能的影响[C].第十四届全国钛及钛合金学术交流会论文集,2010:650-653. |
| [7] | 吴金平;杨英丽;奚正平;孙军.Ti35合金焊接接头在高温硝酸中的腐蚀性能研究[J].钛工业进展,2012(1):22-25. |
| [8] | 宋品玲;吴金平;杨英丽.Ti-6 Ta合金等离子焊焊接接头的组织与性能[J].钛工业进展,2013(6):30-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%