采用复合电沉积的方法,在一定的工艺条件下制备出Ni-SiC复合镀层.通过摩擦磨损试验、电化学腐蚀试验,并利用扫描电镜观察镀层的磨损和腐蚀形貌,综合分析了SiC颗粒大小对镀层性能的影响.结果表明:当SiC粒径为2μm,添加量为60 g·L-1时,镀层的显微硬度最高,耐磨性能最佳;复合镀层的耐蚀性比纯镍镀层和钢基体优越,但随着SiC粒径的增大,镀层的耐蚀性反而有所下降.
参考文献
| [1] | 安茂忠.电镀理论与技术[M].哈尔滨:哈尔滨工业大学出版社,2004:229. |
| [2] | Zhou Y;Zhang H;Qian B .Friction and wear properties of the co-deposited Ni-SiC nanocomposite coating[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(20):8335-8339. |
| [3] | 苏立民,虞润林,吴玉道,李晋,王春亮,薛武智.复合镀技术及其在转子发动机缸体中的应用[J].腐蚀与防护,2005(02):67-68,71. |
| [4] | Hou K H;Ger M D et al.[J].Wear,2002,253:994. |
| [5] | Vaezi MR;Sadrnezhaad SK;Nikzad L .Electrodeposition of Ni-SiC nano-composite coatings and evaluation of wear and corrosion resistance and electroplating characteristics[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2008(1/3):176-182. |
| [6] | 吕柏林.耐磨复合镀层的研究进展[J].电镀与精饰,2007(01):27-31. |
| [7] | 邵光杰,秦秀娟,王海燕,荆天辅,姚枚.离心高速电沉积Ni-SiC复合镀层的研究[J].复合材料学报,2003(05):28-32. |
| [8] | 丁雨田,许广济,戴雷,尹建军,寇生中,喇培清.铝合金表面电沉积Ni-SiC复合镀层的研究[J].机械工程学报,2003(01):128-132. |
| [9] | 程森,王昆林,赵高敏.镍基纳米SiC复合镀层的摩擦学性能[J].清华大学学报(自然科学版),2002(04):516-519. |
| [10] | 林志平,黄新民,舒霞,张志明,单传丽.表面活性剂对Ni-SiC复合电镀的影响[J].金属功能材料,2008(05):20-23. |
| [11] | 孙家枢.金属的磨损[M].北京:冶金工业出版社,1992 |
| [12] | Orlovskaja L et al.[J].Surface and Coatings Technology,1999,111:234. |
| [13] | 白新德.材料腐蚀与控制[M].北京:清华大学出版社,2005:68-70. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%