采用柠檬酸溶胶-凝胶法制备了不同锰掺杂含量的BST陶瓷.研究表明,利用柠檬酸溶胶-凝胶法制备BST陶瓷粉末可以降低BST陶瓷的烧结温度至1250℃,Mn掺杂能明显降低BST陶瓷的铁电性,适量掺杂Mn可以获得具有介电常数适中、介电损耗较小,且室温下具有良好热释电性和探测率优值的BST陶瓷.1%Mn掺杂的BST陶瓷在室温下本征热释电系数γint=610nC/(cm2·K),低频下的探测率优值Fd=88.4×10-6Pa-1/2,可以满足制作热释电探测器的要求.讨论了Mn掺杂BST陶瓷的电畴翻转机制
参考文献
| [1] | A. Ioachim;M.I. Toacsan;M.G. Banciu;L. Nedelcu;A. Dutu;S. Antohe;C. Berbecaru;L. Georgescu;G. Stoica;H.V. Alexandru .Transitions of barium strontium titanate ferroelectric ceramics for different strontium content[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2007(16):6289-6293. |
| [2] | Sharma A;Ban Z G;Alpay S P .[J].Applied Physics Letters,2003,95(07):3618-3625. |
| [3] | 董显林,毛朝梁,姚春华,曹菲,王根水.非制冷红外探测器用热释电陶瓷材料研究进展[J].红外与激光工程,2008(01):37-41. |
| [4] | Jang H M;Jun Y H .[J].Ferroelectrics,1997,193(01):125-140. |
| [5] | Y. Gim;T. Hudson;Y. Fan .Microstructure and dielectric properties of Ba_(1-x)Sr_(x)TiO_(3) films grown on LaAlO_(3) substrates[J].Applied physics letters,2000(8):1200-1202. |
| [6] | 沈彩,刘庆峰,刘茜.柠檬酸-硝酸盐燃烧法制备Ba0.5Sr0.5TiO3介电材料[J].无机材料学报,2004(03):681-685. |
| [7] | 金学淼,姜胜林,张光祖.Mn掺杂对BST热释电陶瓷性能的影响[J].压电与声光,2007(05):577-579. |
| [8] | 杨文,常爱民,杨邦朝.微波烧结法制备Ba0.65Sr0.35TiO3热释电陶瓷[J].红外与毫米波学报,2002(03):171-174. |
| [9] | Liu Shaobo;Liu Meidong;Zeng Yike et al.[J].Materials Science and Engineering B,2002,9(1-2):149-153. |
| [10] | Es-Souni M.;Iakovlev S.;Solterbeck CH. .Multilayer ferroelectric thin films for pyroelectric applications[J].Sensors and Actuators, A. Physical,2003(1/2):114-119. |
| [11] | 张光祖,姜胜林,张洋洋,张清风,张先云.BST陶瓷场致热释电性能的研究[J].压电与声光,2009(04):538-540. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%