采用机械合金化法制备了Mg2Ni-1.0%Pd(质量分数,下同)合金粉末,用XRD及AFM等分析表征了球磨20 h后粉末的相结构和微观形貌,测定了Mg2Ni-1.0%Pd合金吸放氢氘的P-C-T曲线和动力学曲线.结果表明,机械合金化制备的Mg2Ni-1.0%Pd合金粉末粒度在10 nm～50 nm之间;同熔炼法制备的Mg2Ni合金相比,纳米Mg2Ni-1.0%Pd合金吸氢时的焓变值减小,放氢时焓变值增大,可逆贮氢容量为1.06(H/M,原子比,下同);与吸放氢相比,在相同温度下合金吸放氘的坪台压升高,焓变值减小,具有显著的同位素效应.纳米Mg2Ni-1.0%Pd合金的吸氢速率和吸氘速率与温度的关系在573 K附近发生变化.
参考文献
| [1] | Yang Huabin;Yuan Huatang;Ji Jingtao et al.[J].Journal of Alloys and Compounds,2002,330-332:640. |
| [2] | Grigorova E;Khristov M;Khrussanova M et al.[J].Int J Hydrogen Energy,2005,30(10):1099. |
| [3] | Zaluski L;Zaluska A;StrOm-Olsen J O .[J].JOURNAL OF ALLOYS AND COMPOUNDS,1997,217:295. |
| [4] | Janot, R;Aymard, L;Rougier, A;Nazri, GA;Tarascon, JM .Fast hydrogen sorption kinetics for ball-milled Mg2Ni alloys[J].The journal of physics and chemistry of solids,2004(2/3):529-534. |
| [5] | Fukada S;Yamasaki T;Matsuo H et al.[J].International Journal of Hydrogen Energy,1991,16(12):809. |
| [6] | Reilly J J;Wiswall R H .[J].Inorganic Chemistry,1968,7(11):2254. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%