研究了Zr56.6Cu17.3Ni12.5Al9.6Ti4(at.%)块体非晶合金连续升温过程中的晶化行为.结果表明,随着升温速度的增加,特征温度Tg,Tx,Tp1,Tp2均向高温区移动,特征温度与升温速度的关系可以用一次指数衰减关系拟合.采用Kissinger法和Ozawa法分别计算了特征温度对应的激活能Eg,Ex,Ep1,Ep2.由于不同升温速度下特征温度对应的晶化体积分数几乎不变,因而,采用Kissinger法计算结果与Ozawa法的计算结果呈现一致性.Eg1,Ex,Ep1,Ep2之间的大小关系为:Eg≈Ep1≈Ep2＜Ex.
参考文献
| [1] | Johnson W L .[J].MRS Bulletin,1999,24(10):42. |
| [2] | Wang WH;Dong C;Shek CH .Bulk metallic glasses[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(2/3):45-89. |
| [3] | Lu K .[J].Materials Science and Engineering R:Reports,1996,16:161. |
| [4] | 何国 et al.[J].金属学报,1999,35(05):458. |
| [5] | 张庆生,邓玉福,贺连龙,张海峰,丁炳哲,胡壮麒.Zr55Al10Ni5Cu30块状非晶合金靠近玻璃转变点的等温纳米晶化[J].金属学报,2003(03):301-304. |
| [6] | Gogebakan M et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1997,226-228:168. |
| [7] | Hoyer W;Kaban I;Jovari P;Dost E .Crystallization behavior and structure of amorphous Ge15Te85 and Ge20Te80 alloys[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2004(0):565-568. |
| [8] | Gao Y L;Shen J;Sun J F et al.[J].Materials Letters,2003,57:2341. |
| [9] | 邢大伟,沈军,孙剑飞,柳宇,王刚,陈德民.Zr56.6Cu17.3Ni12.5Al9.6Ti4块体非晶合金的玻璃形成能力[J].中国有色金属学报,2004(02):168-172. |
| [10] | 赵德乾,C.H.Shek,汪卫华.Zr-Ti-Cu-Ni-Be-Fe大块非晶合金晶化动力学效应[J].金属学报,2001(07):754-758. |
| [11] | Wang W H et al.[J].Journal of Applied Physics,2000,88:3914. |
| [12] | Liu L;Wu Z F;Zhang J .[J].Journal of Alloys and Compounds,2002,339:90. |
| [13] | Kissinger H E .[J].Analytical Chemistry,1957,29:1072. |
| [14] | 高玉来,沈军,孙剑飞,王刚,陈德民,邢大伟,周彼德.Zr-Al-Ni-Cu大块非晶合金的变温晶化行为研究[J].稀有金属材料与工程,2003(07):518-521. |
| [15] | 李余增.热分析[M].北京:清华大学出版社,1987:82. |
| [16] | G(o)gebakan M;Uzunb O .[J].Journal of Materials Processing Technology,2004,153-154:829. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%