The armour grade quenched and tempered steel joints fabricated using low hydrogen ferritic steel (LHF) filler exhibited superior joint efficiency owing to preferential ferrite microstructure in the welds and also they offered required resistance to HIC. However,the combat vehicles used in military operations will be required to operate under a wide range of road conditions ranging from first class to cross country. Structural components in combat vehicles are subjected to dynamic loading with high strain rates during operation. Stress loadings within the vehicle hull of these vehicles are expected to fluctuate considerably and structural cracking especially in welds during the service life of these vehicles can lead to catastrophic failures. Under these conditions,fracture behaviour of high strain rate sensitive structural steels can be better understood by dynamic fracture toughness (K1d). Hence,an attempt was made to study dynamic fracture toughness of the armour grade quenched and tempered steel and their welds fabricated using LHF consumables. The experimental results indicate that the K1d values of the joints fabricated by shielded metal arc welding (SMAW) are higher than those of the joints fabricated using flux cored arc welding (FCAW) process.
参考文献
| [1] | Gupta B.Indian Armour Steel-A Review[M].Chennai:Combat Vehicle Research Development,1974 |
| [2] | Shah Khan M Z;Alkemade S J;Weston G M et al.Variable-Amplitude Fatigue Testing of High Hardness Armour Steel[J].International Journal of Fatigue,1998,20(03):233. |
| [3] | Rajanna K;Bhambri S K;Achar D R G .An Assessment of a CrMoV Steel Weld Joint for Dynamic Fracture Behaviour[J].Engineering Fracture Mechanics,1988,29(04):387. |
| [4] | Reddy G M;Mohandas T;Sarma D S .Cold Cracking Studies on Low Alloy Steel Weldments:Effect of Filler Metal Composition[J].Sci Tech Weld Join,2003,8(06):407. |
| [5] | G Magudeeswaran,V Balasubramanian,G Madhusudhan Reddy,T S Balasubramanian.Effect of Welding Processes and Consumables on Tensile and Impact Properties of High Strength Quenched and Tempered Steel Joints[J].钢铁研究学报(英文版),2008(06):87-94. |
| [6] | G.Magudeeswaran,V.Balasubramanian,G.Madhusudhan Reddy.Cold Cracking of Flux Cored Arc Welded Armour Grade High Strength Steel Weldments[J].材料科学技术学报（英文版）,2009(04):516-526. |
| [7] | Kobayashi T .Analysis of Impact Properties of A533 Steel for Nuclear Reactor Pressure Vessel by Instrumented Charpy Test[J].Engineering Fracture Mechanics,1984,19(01):49. |
| [8] | Mark-Markowitch M;Rosenthal Y;Adam G .Experience With a Digitized Instrumented Impact Testing System[J].Journal of Testing and Evaluation,1987,15(05):265. |
| [9] | Angamuthu K;Guha B;Achar D R G .Investigation of Dynamic Fracture Toughness (J1d) Behaviour of Strength Mis-Matched Q & T Steel Weldments Using Instrumented Charpy Impact Testing[J].Engineering Fracture Mechanics,1999,64(04):417. |
| [10] | Mohandas T;Madhusudan Reddy G;Satish Kumar B .Heat-Affected Zone Softening in High-Strength Low-Alloy Steels[J].Journal of Materials Processing Technology,1999,88(01):284. |
| [11] | B. BASU;R. RAMAN .Microstructural Variations in a High-Strength Structural Steel Weld under Isoheat Input Conditions[J].Welding Journal,2002(11):(239-S)-(248-S)-0. |
| [12] | WANG JUAN;LI YAJIANG .Microstructure characterization in the weld metals of HQ130 + QJ63 high strength steels[J].Bulletin of Materials Science,2003(3):295-299. |
| [13] | Harrison P;Farrar R .Microstructure and Toughness of C-Mn and CMn-Ni Weld Metal-Part 1[J].Metals Construction,1987,7(02):392R. |
| [14] | Dixon B;Hakansson K .Effect of Welding Parameters on Weld Zone Toughness and Hardness in 690 MPa Steel[J].Welding Journal,1995,74(04):122s. |
| [15] | Ade F .Ballistic Qualification of Armour Steel Weldments[J].Welding Journal,1991,70(01):53. |
| [16] | Ade F .Ballistic Qualification of Armour Steel Weldments[J].Welding Journal,1991,70(01):53. |
| [17] | ASME II C-SFA,5.29.ASME II C-SFA,5.29.Specifications for Low Alloy Steel Electrodes for Flux Cored Metal Arc Welding[S].USA:ASME,2007. |
| [18] | Magudeeswaran G .Fatigue and Fracture Toughness Behaviour of Armour Grade,Quenched and Tempered,High Strength Steel Joints[D].Tamilnadu:Annamalai University,2008. |
| [19] | M. Z. Shah Khan;S. J. Alkemade;G. M. Weston;D. G. Wiese .Variable-amplitude fatigue testing of a high hardness armour steel[J].International Journal of Fatigue,1998(3):233-239. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%