采用程序升温还原法对一系列具有相同W含量和不同Ni含量的硫化态NiW/Al2O3催化剂进行了表征,以考察催化剂中不同硫物种的数量及还原性能. 结果表明,含有助剂Ni的催化剂的TPR谱在673～873 K出现了一个还原峰,归属为催化剂的NiWS混合相被分解生成的硫化镍物种的还原. 随着助剂Ni含量的增加,与该还原峰相应的H2S生成量增大,表明形成了更多的NiWS活性相. 另外,Ni/(Ni+W)原子比为0.41的催化剂样品的噻吩加氢脱硫活性随着还原温度的升高而急剧下降,证实了催化剂在还原过程中活性相被逐步分解.
参考文献
| [1] | Bhatia S;Beltramini J;Do D D .[J].Catalysis Today,1990,7(03):1. |
| [2] | Jones A;McNicol B D.Chemical Industries,Vol 24:Temperature-Programmed Reduction for Solid Materials Characterization[M].New York:Marcel Dekker lnc,1986:76. |
| [3] | Scheffer B;Dekker N J J;Mangnus P J;Moulijn J A .[J].Journal of Catalysis,1990,121(01):31. |
| [4] | Labruyère F;Lacroix M;Schweich D;Breysse M .[J].Journal of Catalysis,1997,167(02):464. |
| [5] | Topsoe H;Clausen B S;Topsoe N-Y;Norskov J K,Ovesen C V,Jacobsen C J H .[J].Bulletin des Societes Chimiques Belges,1995,104(4/5):283. |
| [6] | Jacobsen CJH.;Topsoe H.;Tornqvist E. .HDS, HDN and HYD activities and temperature-programmed reduction of unsupported transition metal sulfides[J].Catalysis Letters,1999(3/4):179-183. |
| [7] | Nag N K;Fraenkel D;Moulijn J A;Gates B C .[J].Journal of Catalysis,1980,66(01):162. |
| [8] | Scheffer B;Molhoek P;Moulijn J A .[J].Applied Catalysis,1989,46(01):11. |
| [9] | Louwers S P A;Prins R .[J].Journal of Catalysis,1993,139(02):525. |
| [10] | Mangnus P J;Bos A;Moulijn J A .[J].Journal of Catalysis,1994,146(02):437. |
| [11] | 左东华,谢玉萍,聂红,石亚华,李灿.4,6-二甲基二苯并噻吩加氢脱硫反应机理的研究Ⅰ. NiW体系催化剂的催化行为[J].催化学报,2002(03):271-275. |
| [12] | 左东华,聂红,Michel Vrinat,石亚华,Michel Lacroix,李大东.硫化态NiW/Al2O3催化剂加氢脱硫活性相的研究Ⅰ.XPS和HREM表征[J].催化学报,2004(04):309-314. |
| [13] | Calais C.;Geantet C.;Yoshimura Y.;Shimada H. Nishijima A.;Lacroix M.;Breysse M.;Matsubayashi N. .Crystallite size determination of highly dispersed unsupported MoS2 catalysts[J].Journal of Catalysis,1998(2):130-141. |
| [14] | Louwers S P A;Prins R .[J].Journal of Catalysis,1992,133(01):94. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%