利用沸石改性磷酸镁水泥,对模拟放射性核素133Cs进行固化,研究了固化体的抗压强度、抗冲击性、抗浸泡性、抗冻融性和抗浸出性,并分析了固化体的物相组成、孔结构和微观形貌.试验结果表明,沸石改性磷酸镁水泥含Cs固化体具有较好的力学性能;掺入沸石改善了固化体的抗冻融性、抗浸泡性和抗浸出性,掺入10％沸石使Cs+的42 d累积浸出分数下降了42.2％,沸石一方面增强了固化体的密实程度,提高了固化体的机械固化能力,另一方面沸石的晶体结构增强了固化体对Cs+的吸附固化能力.
参考文献
| [1] | 陈良;陈莉;李均华.压水堆核电站放射性废液水泥固化技术分析[J].核动力工程,2009(2):113-116,123. |
| [2] | Mestres G;Ginebra MP.Novel magnesium phosphate cements with high early strength and antibacterial properties.[J].Acta biomaterialia,20114(4):1853-1861. |
| [3] | A. Covill;N. C. Hyatt;J. Hill.Development of magnesium phosphate cements for encapsulation of radioactive waste[J].Advances in Applied Ceramics,20113(3):151-156. |
| [4] | Vinokurov, SE;Kulyako, YM;Slyuntchev, OM;Rovny, SI;Myasoedov, BF.Low-temperature immobilization of actinides and other components of high-level waste in magnesium potassium phosphate matrices[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,20091(1):189-192. |
| [5] | 张时豪;汪宏涛;丁建华;姜自超;戴丰乐.磷酸镁水泥应急固化模拟放射性核素90Sr[J].硅酸盐通报,2016(4):1040-1045,1073. |
| [6] | 李全伟;张东;李帆.沸石用于放射性废树脂水泥固化的试验研究[J].非金属矿,2005(5):42-44. |
| [7] | 高亚 .模拟高盐高碱中低水平放射性废液水泥固化技术研究[D].西南科技大学,2014. |
| [8] | 包健.在沸石对高放废液水泥固化体中Cs+浸出率的影响[J].环境科学与技术,2009(07):160-162. |
| [9] | Arun S. Wagh;Seung Y. Jeong.Chemically Bonded Phosphate Ceramics: I, A Dissolution Model of Formation[J].Journal of the American Ceramic Society,200311(11):1838-1844. |
| [10] | 夏锦红;袁大伟;王立久.磷酸镁水泥水化机理研究[J].武汉理工大学学报,2009(9):25-28. |
| [11] | 易发成;李玉香;唐蓉;石正坤;张东.矿物材料对核素Sr、Cs的吸附性能研究[J].中国矿业,2004(12):67-70. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%