Nanocrystalline particles of barium ferrite magnetic material have been prepared by co-precipitation route using aqueous and non-aqueous solutions of iron and barium chlorides with a Fe/Ba molar ratio of 11 and subsequent drying-annealing treatment. Water and ethanol/water mixture with volume ratio of 3:1 were used as solvents in the process. Coprecipitated powders were annealed at various temperatures for 1 h. FTIR (Fourier transform infrared spectroscopy), XRD (X-ray diffraction), DTA/TGA (differential thermal analy-sis/thermogravimetric analysis) and SEM (scanning electron microscopy) techniques were used to evaluate powder particle characteristics. DTA/TGA results confirmed by those obtained from XRD indicated that the formation of barium ferrite occurs in sample synthesized in ethanol/water solution at a relatively low temperature of 631℃. Nano-size particles of barium ferrite with mean particle size of almost 75 and 100 nm were observed in the SEM micrographs of the samples synthesized in ethanol/water solution after annealing at 700 and 800℃ for 1 h, respectively.
参考文献
| [1] | H Kojima;E P Wohl-farth.Ferromagnetic Materials[M].Amsterdam:North-Holland Publishing Company,1982:305. |
| [2] | G. Benito;M.P. Morales;J. Requena;V. Raposo;M. Vazquez;J.S. Moya .Barium hexaferrite monodispersed nanoparticles prepared by the ceramic method[J].Journal of Magnetism and Magnetic Materials,2001(1):65-72. |
| [3] | M Rozman;M Drofenik .[J].Journal of the American Ceramic Society,1998,81:1757. |
| [4] | A Ataie;S Heshmati-Manesh;H Kazempour .[J].Journal of Materials Science,2002,37:2125. |
| [5] | G V Duong;R S Turtelli;B D Thuan;D V Linh N Hanh R Groessinger .[J].Journal of Non-Crystalline Solids,2007,353:811. |
| [6] | J Palla;D O Shah;P G Casillas;J M Aquino .[J].Journal of Nanoparticle Research,1999,1:215. |
| [7] | R Muller;C Ulbrich;W Schuppel;H Steinmetz E Steinbei .[J].Journal of the European Ceramic Society,1999,19:1547. |
| [8] | G M Suarez;M C Morales;M M Guerrero;K K Johal H M Molinar O E Valenzuela J I Garcia .[J].Materials Chemistry and Physics,2002,77:796. |
| [9] | H L Su;Y Xie;B Li;X M Liu Y T Qian .[J].Journal of Solid State Chemistry,1999,146:110. |
| [10] | D Lisjak;M Drofenik .[J].Journal of the European Ceramic Society,2006,26:3681. |
| [11] | B D Cullity.Elements of X-ray Diffraction[M].Massachusetts:Addison-Wesley,1978 |
| [12] | M S Kaliszewski;A H Heuer .[J].Journal of the American Ceramic Society,1990,73:1504. |
| [13] | J A Gadsden.Infrared Spectra of Minerals and Related Inorganic Compounds[M].Butterworth Ltd,USA,1975 |
| [14] | H Hsiang;R Q Yao .[J].Materials Chemistry and Physics,2007,104:1. |
| [15] | F A Miller;C H Wilkins .[J].Analytical Chemistry,1952,24:1253. |
| [16] | S Wang;Y Zhai;X Li;Y Li K Wang .[J].Journal of the American Ceramic Society,2006,89:3577. |
| [17] | R.C. Pullar;A.K. Bhattacharya .Crystallisation of hexagonal M ferrites from a stoichiometric sol―gel precursor, without formation of the α-BaFe_2O_4 intermediate phase[J].Materials Letters,2002(3):537-542. |
| [18] | K. Sheikhi Moghaddam;A. Ataie .Role of intermediate milling in the processing of nano-size particles of barium hexaferrite via co-precipitation method[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2006(1/2):415-419. |
| [19] | M Readey;R Lee;J Halloran;A Heuer .[J].Journal of the American Ceramic Society,1990,73:1499. |
| [20] | J Ding;D Maurice;W F Miao;P G McCormick R Street .[J].Journal of Magnetism and Magnetic Materials,1995,150:417. |
| [21] | O Carp;R Barjega;E Segal;M Brezeanu .[J].Thermochimica Acta,1998,318:57. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%