通过熔融盐法以BaC_2O_4、TiO_2为前驱体,NaCl为熔盐制备了BaTiO_3粉体.SEM分析所得样品为立方状颗粒,粒径为50～300nm,采用Rietveld全谱拟合法对其物相组成进行了分析,并通过变温XRD对BaTiO_3相变进行了表征,Rietveld全谱拟合结果表明,该方法制备的BaTiO_3粉体在室温下是一种四方、立方混合相,质量分数分别为73.9%、26.1%.精修结果的数值判据分别为:加权剩余方差因子R_(wp)=5.93%、剩余方差因子R_p=4.78%、拟合优值S(Goodness of fit)=1.53.变温XRD研究表明所制备的BaTiO_3粉体具有四方到立方相的相变.
BaTiO_3 particles are synthesized using BaC_2O_4 and TiO_2 powders as precursors and NaCl as molten flux through a molten salt method.SEM characterization illustrates that the BaTiO_3 particles have a cubic shape and with a size about 50～300nm.The phase composition of the obtained product has been determined using the Rietveld refinement method.XRD at several temperatures is taken to investigate the phase transition of the product.The Rietveld refinement result reveals that the product is made up of a mixture of tetragonal and cubic phases.The mass fraction of tetragonal and cubic phases is 73.9% and 26.1%,respectively.The reliability factors of the refinement are R_(wp)=5.93%,R_p=4.78%,S(goodness of fit)=1.53.Temperature variable XRD reveals that the obtained BaTiO_3 particles have a tetragonal-to-cubic structural phase transition.
参考文献
| [1] | 全学军,蒲昌亮.钛酸钡的制备研究进展[J].材料导报,2002(06):45-47,67. |
| [2] | Joshi UA;Yoon SH;Baik SG;Lee JS .Surfactant-free hydrothermal synthesis of highly tetragonal barium titanate nanowires: A structural investigation[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2006(25):12249-12256. |
| [3] | Liu D;Yan YK;Zhou HP .Synthesis of micron-scale platelet BaTiO3[J].Journal of the American Ceramic Society,2007(4):1323-1326. |
| [4] | Reza Asiaie;Weidong Zhu;Sheikh A. Akbar;Prabir K. Dutta .Characterization of Submicron Particles of Tetragonal BaTiO_3[J].Chemistry of Materials,1996(1):226-234. |
| [5] | Zhu X H;Wang J Y;Zhang Z H et al.Atomic-scale characterization of barium titanate powders formed by the hydrothermal process[J].Journal of the American Ceramic Society,2008,91(03):1002. |
| [6] | Rietveld H M .Line profiles of neutron powder-diffraction peaks for structure refinement[J].Acta Crystallographica,1967,22:151. |
| [7] | Hill R J;Howard C J .Quantitative phase-analysis from neutron powder diffraction data using the rietveld method[J].Journal of Applied Crystallography,1987,20:467. |
| [8] | Bish D L;Howard S A .Quantitative phase-analysis using the rietveld method[J].Journal of Applied Crystallography,1988,21:86. |
| [9] | McCusker L.B.;Von Dreele R.B.;Cox D.E.;Louer D.;Scardi P. .Rietveld refinement guidelines[J].Journal of Applied Crystallography,1999(1):36-0. |
| [10] | 曾令民,杨喜英,王力珩,李小萍,葛宪民.X射线衍射里特沃尔德全谱图拟合法测定粉尘中游离的SiO2[J].分析化学,2008(05):599-603. |
| [11] | 王超群,王宁,李娜娜.Rietveld 分析方法在钨冶金氧化物相定量分析中的应用[J].硬质合金,2003(02):104-108. |
| [12] | Akdogan E K;Safari A .Phenomenological theory of size effects on the cubic-tetragonal phase transition in BaTiO_3 nanocrystals[J].Japanese Journal of Applied Physics Part 1:Regular Papers and Short Notes and Review Papers,2002,41(11B):7170. |
| [13] | 宋红章,李永祥,殷庆瑞.铁电体中相变临界尺寸的研究现状[J].无机材料学报,2007(04):583-589. |
| [14] | Qing Huang;Lian Gao .Multiwalled carbon nanotube/BaTiO_(3) nanocomposites: Electrical and rectification properties[J].Applied physics letters,2005(12):123104-1-123104-3-0. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%