采用钛酸酯对滑石粉进行表面改性,以接触角为评价指标,得到最佳的改性工艺参数为:钛酸酯的添加量为3％,反应温度为65℃,反应时间为1.5h.分别采用粒度分析、XRD分析、红外光谱分析以及热重分析对改性前后滑石粉的结构和表面性质进行表征,结果表明,钛酸酯对滑石粉的改性效果显著,表面改性过程不仅发生了物理吸附,还存在化学键合.
参考文献
| [1] | Castillo, L.A.;Barbosa, S.E.;Maiza, P.;Capiati, N.J..Surface modifications of talcs. Effects of inorganic and organic acid treatments[J].Journal of Materials Science,20118(8):2578-2586. |
| [2] | Weon JI;Sue HJ.Mechanical properties of talc- and CaCO3-reinforced high-crystallinity polypropylene composites[J].Journal of Materials Science,20068(8):2291-2300. |
| [3] | B. K. Prasad;S. Rathod;O. P. Modi;M. S. Yadav.Influence of talc concentration in oil lubricant on the wear response of a bronze journal bearing[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20105/6(5/6):498-505. |
| [4] | 李丽匣;韩跃新;陶世杰.碳酸钙晶须表面改性研究[J].化工矿物与加工,2008(5):4-8. |
| [5] | 林轩;张平民;尹周澜;陈启元;梁跃杰.纳米SnO2的表面改性研究[J].化工进展,2005(4):395-398. |
| [6] | 刘铭;霍冀川;刘树信.硬脂酸对碳酸钡表面改性的研究[J].中国粉体技术,2011(6):58-62. |
| [7] | 郝书峰;郑治祥;范卫青;徐光青;吕珺;吴玉程.沉淀法白炭黑的表面改性及其性能研究[J].硅酸盐通报,2011(3):529-533. |
| [8] | 姚超;左士祥;杜郢;汪信;陈天虎.凹凸棒石的表面改性及其在脲醛树脂中的应用[J].硅酸盐学报,2011(4):630-634. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%