在微波辐射下进行甲基丙烯酸甲酯(MMA)的无乳化剂乳液聚合.发现在微波辐照下MMA聚合速率较加热有较大的提高.微波辐照制备的聚甲基丙烯酸甲酯(PMMA)乳液粒子形状规整,粒径分散系数1.03,达到单分散要求.微波制备乳液的数均分子量与常规加热接近,但分子量分布变窄.微波和热无乳化剂聚合的PMMA的热解过程一致,在200 ℃～390 ℃有三个分解峰,与有乳化剂聚合有很大差异.FT-IR、13C-NMR表明无乳化剂聚合的PMMA序列结构以间同为主,微波聚合略微降低PMMA的立构规整度.
参考文献
| [1] | Correa R.;Dougar V.;Gonzalez G. .Emulsion polymerization in a microwave reactor[J].Polymer: The International Journal for the Science and Technology of Polymers,1998(6-7):1471-1474. |
| [2] | Palacios F;Valverde C .[J].New Polymeric Materials,1996,5(01):93. |
| [3] | Zhang W M;Gao J;Wu C .[J].Macromolecules,1997,30(20):6388. |
| [4] | Wu C;Gao J;Li M et al.[J].Macromolecular Symposia,2000,150:L219. |
| [5] | Fitch R M.[J].Journal of Polymer Science,1969:2795. |
| [6] | Goodall A R.[J].Journal of Colloid and Interface Science,1979(01):1. |
| [7] | 许涌深,袁才登,王艳君,曹同玉,曹平.无皂乳液共聚合的动力学和机理[J].高分子材料科学与工程,2000(01):46-48,52. |
| [8] | Takashi K .[J].Macromolecules,1986,19(08):2160. |
| [9] | Enzo G;Romano M .[J].Journal of Polymer Science Part A:Polymer Chemistry,1986,24(10):2517. |
| [10] | Dybal J;Stoker J;Schneider B .[J].Polymer,1983,24:971. |
| [11] | Allen P et al.[J].European Polymer Journal,1985,21(07):603. |
| [12] | Dirlikov S et al.[J].Applied Spectroscopy,1979,33(06):551. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%