以ZrO(NO3)2和N6H24Mo7O24·4H2O等为原料,采用湿化学法制备出立方相ZrMo2O8粉体.对前驱体在室温～800℃进行了TG-DSC测试,采用XRD、SEM对立方相ZrMo2O8粉体进行了分析观测.结果表明:亚稳相立方ZrMo2O8的制备对热处理工艺十分敏感,采用湿化学法在450℃制各出单一立方相ZrMo2O8粉体,在室温～400℃热膨胀系数为-4.337×10-6K-1.
参考文献
| [1] | Evans J S O et al.[J].Chemistry of Materials,1996,8:2809. |
| [2] | Mary T A et al.[J].Science,1996,272:90. |
| [3] | 沈容,王天民.Al2Mo3-xWxO12的合成及热膨胀特性的研究[J].稀有金属材料与工程,2004(01):91-95. |
| [4] | Sleight A W .[J].Synthesis and Reactivity of Solids,1998,3:128. |
| [5] | Andraej Grzechnik;Wilson A Crichton .[J].Solid State Sciences,2002,4:1137. |
| [6] | Simon Allen;Nicholas R Warmingham .[J].Chemistry of Materials,2003,15:3406. |
| [7] | Lind C.;Hu ZB.;Short S.;Jorgensen JD.;Wilkinson AP. .Synthesis and properties of the negative thermal expansion material cubic ZrMo2O8[J].Chemistry of Materials,1998(9):2335-2337. |
| [8] | 沈容 .Investigation on New Type Negative Thermal Expansion Oxide Materials[D].北京:北京航空航天大学,2002. |
| [9] | Lind C;Wilkinson A P;Rawn C J et al.[J].MATERIALS CHEMISTRY,2001,11:3354. |
| [10] | 杨南如.Test Method of Inorganic Non-metal Material[M].武汉:武汉理工大学出版社,2000 |
| [11] | 王明松,张跃,宋强,王聪.负热膨胀材料立方ZrMo2O8合成研究[J].中国稀土学报,2003(z1):94-97. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%