为实现高强韧超细晶AZ91D镁合金的有效防护,利用硅酸盐电解液对其进行微弧氧化(MAO).分析了工作电压、频率、占空比和氧化时间对所得膜层耐蚀性的影响,通过正交试验优选出MAO工艺,其参数如下:正电压400 V,负电压-15 V,频率600Hz,占空比30％,氧化时间20 min.与常规MAO工艺相比,该MAO膜厚度达到19.23μm,表面孔隙率约为8.3％,且点蚀电位更高(-0.199 V相对于SCE)、阻抗值更大(776.5 kΩ·m2)、有效保护时间延长了1.29倍.
参考文献
| [1] | 师昌绪,李恒德,王淀佐,李依依,左铁镛.加速我国金属镁工业发展的建议[J].材料导报,2001(04):5-6. |
| [2] | Xi-Shu Wang;Li Jin;Ying Li;Xing-Wu Guo .Effect of equal channel angular extrusion process on deformation behaviors of Mg-3Al-Zn alloy[J].Materials Letters,2008(12/13):1856-1858. |
| [3] | Chen B;Lin DL;Jin L;Zeng XQ;Lu C .Equal-channel angular pressing of magnesium alloy AZ91 and its effects on microstructure and mechanical properties[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(0):113-116. |
| [4] | D. Song;A.B. Ma;J.H. Jiang;P.H. Lin;D.H. Yang;J.F. Fan .Corrosion behaviour of bulk ultra-fine grained AZ91D magnesium alloy fabricated by equal-channel angular pressing[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(1):362-373. |
| [5] | 黄光胜,范永革,汤爱涛,汪凌云.镁及镁合金腐蚀最新研究进展[J].材料导报,2002(04):38-40. |
| [6] | 蒋百灵,张淑芬,吴国建,雷廷权.镁合金微弧氧化陶瓷层显微缺陷与相组成及其耐蚀性[J].中国有色金属学报,2002(03):454-457. |
| [7] | 张先锋,蒋百灵.能量参数对镁合金微弧氧化陶瓷层耐蚀性的影响[J].腐蚀科学与防护技术,2005(03):141-143. |
| [8] | 王燕华,王佳,张际标.电流密度对AZ91D镁合金微弧氧化膜性能的影响[J].中国腐蚀与防护学报,2005(06):332-335. |
| [9] | 刘全心 .电参数对镁合金微弧氧化膜层的显微结构和耐蚀性能的影响[D].华中科技大学,2005. |
| [10] | 姚美意,周邦新,王均安.电压对镁合金微弧氧化膜组织及耐蚀性的影响[J].材料保护,2005(06):7-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%