碳包覆纳米SnO2锂离子电池负极材料合成及其性能研究

无机材料学报, 2009, 24(1): 147-151.

碳包覆纳米SnO2锂离子电池负极材料合成及其性能研究

杨同欢 ^1, , 郭永榔 ^2, , 周学酬 ^3, , 刘永梅 ^4,

1.福州大学,化学化工学院,福州,350108

2.福州大学,化学化工学院,福州,350108

3.福州大学,化学化工学院,福州,350108

4.福州大学,化学化工学院,福州,350108

关键词：锂离子电池 , 负极 , SnO2 , 无定形碳包覆

Preparation of Amorphous Carbon-coated Nano-scale SnO2 and its Performance for Anode Material of Lithium Ion Secondary Battery

采用热解Sn(OH)4和淀粉混合物制备碳包覆纳米SnO2的方法合成了无定形碳包覆纳米SnO2.采用XRD、SEM、TEM、STEM-EDX以及充放电测试等手段对其结构、形貌和性能进行表征.结果表明,样品材料中无定形碳呈薄片状,被包覆的纳米SnO2(20～50nm)均匀分布在片状无定形碳中.产物中SnO2与碳的不同比例影响了产物的性能,样品(SnO2∶ C＝1∶ 1)首次循环的可逆比容量达到404mAh·g-1,20次循环内无明显衰减.

参考文献

[1]	Nam S C,Yoon Y S,Cho W I,et al.Electrochem.Commun.,2001,3(1):6-10.
[2]	Poizot P,Grugeon S,Grugeon S,et al.Nature,2000,407(6803):496-499.
[3]	Gao X P,Bao J L,Pan G L,et al.J.Phys.Chem.B,2004,108(18):5547-5551.
[4]	Xia Y Y,Sakai T,Fujieda T,et al.J.Electrochem.Soc.,2001,148(5):A471-A481.
[5]	Lee H Y,Jang S W,Lee S M,et al.J.Power Sources,2002,112(1):8-12.
[6]	Dong Q F,Wu C Z,Jin M G,et al.Solid State Ionics,2004,167(1-2):49-54.
[7]	Chiu K F,Liu K M,Lin H C,et al.J.Electrochem.Soc.,2007,154(5):A433-A437.
[8]	Tamura T,Kato Y,Mikami A,et al.J.Electrochem.Soc.,2006,153(12):A2227-A2231.
[9]	Park M S,Kang Y M,Kim J H,et al.Carbon,2008,46(1):35-40.
[10]	Yuan L,Wang J,Chew S Y,et al.J.Power Sources,174(2):1183-1187.
[11]	Wang T,Ma Z N,Xu F,et al.Electrochem.Commun.,2003,5(7):599-602.
[12]	Li H,Huang X,Chen L.Solid State Ionics,1999,123(1-4):189-197.
[13]	何则强,熊利芝,肖卓炳,等(HE Ze-Qiang,et al).无机材料学报(Journal of Inorganic Materials),2006,22(2):253-257.
[14]	Courtney I A,Dahn J R.J.Electrochem.Soc.,1997,144(6):2045-2050.
[15]	Brousse T,Retoux R.J.Electrochem.Soc.,1998,145(1):1-4.
[16]	Whitehead A H,Elliott J M,Owen J R.J.Power Sources,1999,81-82:33-38.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

碳包覆纳米SnO2锂离子电池负极材料合成及其性能研究

Preparation of Amorphous Carbon-coated Nano-scale SnO2 and its Performance for Anode Material of Lithium Ion Secondary Battery

参考文献