在颜料总吸油量一定、各配方中颜料体积浓度(PVC)与临界颜料体积浓度(CPVC)之比为0.77的条件下,通过盐雾试验、极化曲线、开路电位(OCP)-时间曲线和电化学阻抗谱(EIS)研究了片状锌粉取代醇溶性无机富锌涂料中少量球状锌粉对涂层性能的影响.研究结果表明,在片状锌粉取代比为5％ ～ 30％范围内,涂层的耐盐水和耐盐雾腐蚀时间随片状锌粉取代比的增加而先增加后减少,在取代比为20％时达到最大值.与未取代涂层相比,取代比为20％的涂层其牺牲阳极保护时间更长,阳极溶解性能更好,低频(0.2 Hz)阻抗更小.
参考文献
| [1] | 杨振波,李运德,杨忠林,郭万生,师华.片状锌粉在富锌涂料领域的应用及其技术发展趋势[J].电镀与涂饰,2011(02):62-67. |
| [2] | VILCHE J R;BUCHARSKY E C;GI(U)DICE C A .Application of EIS and SEM to evaluate the influence of pigment shape and content in ZRP formulations on the corrosion prevention of naval steel[J].Corrosion Science,2002,44(06):1287-1309. |
| [3] | Jagtap RN;Nambiar R;Hassan SZ;Malshe VC .Predictive power for life and residual life of the zinc rich primer coatings with electrical measurement[J].Progress in Organic Coatings: An International Review Journal,2007(4):253-258. |
| [4] | Kalendova A. .Effects of particle sizes and shapes of zinc metal on the properties of anticorrosive coatings [Review][J].Progress in Organic Coatings: An International Review Journal,2003(4):324-332. |
| [5] | 韩凤俊,周钰明,汪小舟.鳞片状锌粉防腐蚀涂料的研制[J].腐蚀与防护,2006(03):109-112,117. |
| [6] | 李艳云;蔡晓兰;段昕辉.片状锌粉在有机富锌涂料中的应用研究[J].电镀与涂饰,2008(03):24-26. |
| [7] | 张留艳,江静华,马爱斌,杨东辉.硅丙乳液在鳞片状无机富锌涂料中的应用[J].腐蚀科学与防护技术,2010(02):142-145. |
| [8] | 张曾生,熊金平,左禹.片状无机富锌涂料的制备及其性能[J].北京化工大学学报（自然科学版）,2007(z2):69-72. |
| [9] | 杨振波,杨忠林,郭万生,李运德,师华.鳞片型醇溶性无机富锌涂料的研制及其防腐蚀性的研究[J].上海涂料,2010(01):1-4. |
| [10] | 杨振波,杨忠林,郭万生,宋广成.鳞片状富锌涂层耐蚀机理的研究[J].中国涂料,2006(01):19-21. |
| [11] | Subrahmanya Shreepathi;Priyansh Bajaj;B. P. Mallik .Electrochemical impedance spectroscopy investigations of epoxy zinc rich coatings: Role of Zn content on corrosion protection mechanism[J].Electrochimica Acta,2010(18):5129-5134. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%