通过过热蒸气活化法制备的柏木炭中含有大量的中孔,可用于制备以1 mol/L硫酸为电解液的双电层电容器(EDLCs).在50 mA/g电流密度下,柏木炭的质量比电容(C50)为190 F/g;在1 000 mA/g电流密度下,其质量比电容(C1000)为140 F/g.按C1000/C50定义的性能倍率约为0.72.测得的高电容量可归因于微孔和大孔所造成表面的贡献.以简易浸泡法负载少量NiO粒子后,柏木炭的质量比电容可以提高约13%,体积比电容提高约27%,而其性能倍率保持不变.
Cypress charcoals, which were prepared under super-heated steam and had a relatively large amount of mesopores, were used in electric double layer capacitors (EDLCs) in 1 mol/L H2SO4 electrolyte. The gravimetric capacitance of cypress charcoals was about 190 F/g at a current density of 50 mA/g (C50) and 140 F/g at 1 000 mA/g (C1000) and the performance rating defined by C1000/C50 was about 0.72. The capacitance observed was explained by the contributions from the surfaces from the micropores and the larger pores. By loading minute NiO particles through a simple impregnating process, the capacitance of the loaded charcoals was enhanced by about 13% in gravimetric capacitance and by about 27% in volumetric capacitance and the performance rating was kept the same.
参考文献
| [1] | Eiki Ito,Ikuyoshi Kouchi,Sylwia Mozia,Masaharu Okuda,Takashi Nakano,Masahiro Toyoda,Michio Inagaki.由柏木制备纳米孔结构炭材料Ⅰ.制备与孔结构[J].新型炭材料,2007(03):199-205. |
| [2] | Sanada Y;Suzuki M;Fujimoto K.Activated carbons:Fundamentals and Applications[M].Koudansha,1992 |
| [3] | Radovic L R;Moreno-Castilla C;Rivera-Utrilla J .Carbon materials as adsorbents in aqueous solutions[J].Chemistry and Physics of Carbon,2001,27:227-405. |
| [4] | Ikuo Abe .Carbonization and activation techniques for production of carbonaceous adsorbent[J].炭素,2004(211):21-29. |
| [5] | R. Asakura;T. Kondo;M. Morita .Electric double-layer capacitor characteristics of activated wood charcoals[J].炭素,2004(215):231-235. |
| [6] | Kim Y J;Tantrakarn K;Abe Y.Correlation between the capacitor performance and pore structure[J].Tanso,2006(221):31-39. |
| [7] | M. Inagaki;S. Kobayashi;F. Kojin .Pore structure of carbons coated on ceramic particles[J].Carbon: An International Journal Sponsored by the American Carbon Society,2004(15):3153-3158. |
| [8] | Morishita T;Suzuki T;Nishikawa T.Preparation of porous carbons by the carbonization of the mixtures of the thermoplastic precursors with MgO[J].Tanso,2005(219):226-231. |
| [9] | Morishita T;Suzuki T;Nishikawa T.Preparation of mesoporous carbons by carbonization of the mixtures of poly(vinyl alcohol) with magnesium salts[J].Tanso,2006(223):220-226. |
| [10] | Morishita T;Ishihara K;Kato M.Mesoporous carbons prepared from mixtures of magnesium citrate with poly (vinyl alcohol)[J].Tanso,2007(226):19-24. |
| [11] | Michio Inagaki;Masaya Kato;Takahiro Morishita .Direct preparation of mesoporous carbon from a coal tar pitch[J].Carbon: An International Journal Sponsored by the American Carbon Society,2007(5):1121-1124. |
| [12] | T. Morishita;Y. Soneda;T. Tsumura .Preparation of porous carbons from thermoplastic precursors and their performance for electric double layer capacitors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(12):2360-2367. |
| [13] | Takahiro Morishita;Kaori Ishihara;Masaya Kat .Preparation of a carbon with a 2 nm pore size and of a carbon with a bi-modal pore size distribution[J].Carbon: An International Journal Sponsored by the American Carbon Society,2007(1):209-211. |
| [14] | Conway B E;Birss V;Wojtowicz J .The role and utilization of pseudocapacitance for energy storage by supercapacitors[J].Journal of Power Sources,1997,66:1-14. |
| [15] | Yuichi Sato;Koichi Yomogida;Takeshi Nanaumi;Koichi Kobayakawa;Yasuhiko Ohsawa;Mikio Kawai .Electrochemical Behavior of Activated-Carbon Capacitor Materials Loaded with Ruthenium Oxide[J].Electrochemical and solid-state letters,2000(3):113-116. |
| [16] | Ramani M;Haran B S;White R E et al.Studies on activated carbon capacitor materials loaded with different amounts of ruthenium oxide[J].Journal of Power Sources,2001,93:209-214. |
| [17] | Shiraishi S;Kurihara H;Shi L et al.Electric double-layer capacitance of meso/macroporous activated carbon fibers prepared by the blending method I.Nickel-loaded activated carbon fibers in propylene carbonate solution containing LiClO4 salt[J].Journal of the Electrochemical Society,2002,149:A855-A861. |
| [18] | Reddy R N;Reddy R G .Sol-gel MnO2 as an electrode material for electro-chemical capacitors[J].Journal of Power Sources,2003,124:330-337. |
| [19] | Takahiro Morishita;Yasushi Soneda;Hiroaki Hatori;Michio Inagaki .Carbon-coated tungsten and molybdenum carbides for electrode of electrochemical capacitor[J].Electrochimica Acta,2007(7):2478-2484. |
| [20] | Shi H .Activated carbons and double layer capacitance[J].Electrochimica Acta,1996,41:1633-1639. |
| [21] | Grazyna Gryglewicz;Ewa Lorenc-Grabowska;Grzegorz Lota;Elzbieta Frackowiak .Effect of pore size distribution of coal-based activated carbons on double layer capacitance[J].Electrochimica Acta,2005(5):1197-1206. |
| [22] | Lihong Wang;Masahito Fujita;Michio Inagaki .Relationship between pore surface areas and electric double layer capacitance in non-aqueous electrolytes for air-oxidized carbon spheres[J].Electrochimica Acta,2006(19):4096-4102. |
| [23] | Ito E;Nakamura H;Inagaki M.Preparation of porous carbons from cypress using super-heated steam III.Performance in electric double layer capacitor[J].Tanso |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%