以高氯酸为催化剂,乙酸酐为促进剂及分子量调节剂,通过四氢呋喃阳离子开环聚合合成了分子量可控且分子量分布较窄(Mw/Mn＜1.2)的聚四氢呋喃,聚合产物端部含有乙酸酯基,经醇解后得到端羟基聚四氢呋喃(PTMEG).探讨了聚合时间、高氯酸用量、乙酸酐用量、溶剂对聚四氢呋喃分子量(Mn)及分子量分布(Mw/Mn)的影响.研究表明,延长聚合时间、增加高氯酸及乙酸酐的用量均会造成Mn先升后降,但只有聚合时间对Mw/Mn会造成显著的影响,聚合时间为4h时Mw/Mn最小；加入CH2Cl2溶剂会降低聚四氢呋喃的Mn及Mw/Mn.采用凝胶渗透色谱-多角度激光散射联用仪(SEC- MALLS)对聚合产物的Mn及Mw/Mn进行了准确地测定,应用FT-IR、1H-NMR表征了端羟基聚四氢呋喃大分子结构,利用DSC及TG研究了其热性能,结果表明,端羟基聚四氢呋喃的熔点及分解温度随着Mn的增加略有升高.
参考文献
| [1] | 刘志豪;孙经武 .聚四氢呋喃催化合成研究进展[J].弹性体,1999,9(01):41. |
| [2] | 孙亚斌,周集义.四氢呋喃均聚醚催化研究进展[J].化学推进剂与高分子材料,2004(02):7-12. |
| [3] | 俞国星,范晓东,张翔宇,孔杰.窄分子量分布聚四氢呋喃的合成[J].合成化学,2006(05):450-453,467. |
| [4] | Smith S;Hubin A J .The preparation and chemistry of dicationically active polymers of tetrahydrofuran[J].J Macromolecular Sci Part A,1973,7(07):1399. |
| [5] | De Witte I C;Goethals E J .Synthesis and block-specific complexation of poly (ethylene oxide)-poly (tetrahydrofuran)-poly (ethylene oxide) triblock copolymers[J].Polymers For Advanced Technologies,1999,10(05):287. |
| [6] | Pomel C;Leborgne C;Cheradame H;Scherman D;Kichler A;Guegan P .Synthesis and evaluation of amphiphilic poly(tetrahydrofuran-b-ethylene oxide) copolymers for DNA delivery into skeletal muscle.[J].Pharmaceutical research,2008(12):2963-2971. |
| [7] | WANG Guojian,YAN Deyue.Synthesis and characterization of amphiphilc block copolymer poly(methyl acrylic acid)-block-polytetrahydrofuran[J].科学通报（英文版）,2000(21):1948-1952. |
| [8] | Mccarthy B J;Hogen-Esch T E .Synthesis of narrow distribution poly (tetrahydrofuran) initiated by alkylboron triflates[J].Macromolecules,1996,29(08):3035. |
| [9] | Samsonova T I;Mikhailov G D et al.Polymerization of tetrahydrofuran in the presence of acetic anhydride and perchloric acid[J].Fibre Chemistry,1984,15(05):349. |
| [10] | 徐兆瑜.聚四氢呋喃醚二醇的合成和应用[J].化工科技市场,2004(03):1-4. |
| [11] | Sugawara M;Sato M .Reaction of tetrahydrofuran and acetic anhydride catalyzed by electrogenerated acid[J].山形大学纪要工学,1987,19(02):143. |
| [12] | 程时远;李建宗;徐祖顺.端羟基聚四亚甲基醚的制备[J].塑料工业,1989(05):14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%