论述了锆包壳产生碘致应力腐蚀的原因,综述了碘致应力腐蚀的开裂机理和碘致应力腐蚀的影响因素,指出碘致应力腐蚀的影响因素包括:温度、微结构、碘分压和化学因素.
参考文献
| [1] | JacquesP;Lefebvre F et al.Deformation-corrosion interactions for Zr alloys during I-SCC crack initiation part Ⅰ:chemical contributions[J].Journal of Nuclear Materials,1999,264(02):239. |
| [2] | Cox .Pellet clad interation (PCI)failures of zircaloy fuel cladding ,a review[J].Journal of Nuclear Materials,1990,172(08):249. |
| [3] | VidemK;Lunde L .Fuel element failures caused by iodine stress corrosion[J].Annals of Nuclear Energy,1976,3:305. |
| [4] | VidemK;Lunde L;Hollowell T .Cracking of cladding tubes caused by power ramping and by laboratory stress corrosion experiments[J].Journal of Nuclear Materials,1979,87(12):259. |
| [5] | MattasRF;Yaggee F L;Neimark L A.[A].ASTM STP 754,american society for testing and materials,1982:158. |
| [6] | Gartner M;LaVake J C.Power ramp testing and nondestructive post-irradiation examinations of high burnup PWR fuel rods[A].Seattle,1983:254. |
| [7] | PeehsM;Steinberg E;Stehle H.Investigation of stress corrosion cracking in zircaloy tubing with respect to the PCI phenomenon Transaction of the international conference on structural mechanics in reactor technology[A].,1981:6. |
| [8] | KnaaH;Gartner M;Sontheimer F.Proceeding of the IAEA meeting on pellet-cladding iteraction and load-following behavior of water reactor fuel[J].Lyon,1987 |
| [9] | DaviesJH;Rosenbaum H S.Proceedings of the ANS topical meeting on water reactor fuel performance[C].ANSSt Charles IL,1977:230. |
| [10] | KleykampH .Chemical state of the fission products in oxide fuels[J].Journal of Nuclear Materials,1985,131(04):221. |
| [11] | CuicciottiD;JonesRL;Yreet B C S.Chemical aspects of iodine-induced stress corrosion cracking of zircaloys[J].ASTM special technical publication,1982:146. |
| [12] | SidkyPS .Iodine stress corrosion cracking of zircaloy reactor cladding iodine chemistry[J].Journal of Nuclear Materials,1998,256(07):2. |
| [13] | TasoojiA.Modeling of zircaloy stress-corrosion cracking: texture effects and dry storage spent fuel behavior[A].American Society for Testing and Materials,1984:595. |
| [14] | VanderSchaaf .Effect of neurton irradiation on fatigue and fatigue-creep behavior of structural materials[J].Journal of Nuclear Materials,1988,155-157(07):156. |
| [15] | CuicciottiD .Characterization of deposits on inside surfaces of lwr cladding[J].Journal of Nuclear Materials,1978,78(11):96. |
| [16] | WoodJC .Factors affecting stress corrosion cracking of zircaloy in iodine vapour[J].Journal of Nuclear Materials,1972,45(11):105. |
| [17] | DamsonR .Effect of texture on stess corrosion cracking of irradiated zircaloy in iodinie[J].Journal of Nuclear Materials,1980,92(2-3):363. |
| [18] | HaddadR;Cox B .On the initiation of cracks in zircaloy tubes by I2 and Cs/Cd vapours[J].Journal of Nuclear Materials,1986,138(01):81. |
| [19] | LynchS.Stress corrosion cracking and liquid metal embrittlement in pure magnesium[A].Metallogr Soc Toronto,1988:113. |
| [20] | TomalinDS.Localized ductility of irradiated zorcaloy-2cladding in air and iodine environments[J].zirconium in the nuclear industry ASTM STP 633 american society for testing Materials,1977:568. |
| [21] | VidemK;Lunde L .Cracking of cladding tubes caused by power ramping and by laboratory stress corrosion experiments[J].Journal of Nuclear Materials,1979,87(02):259. |
| [22] | Cox;Wood J C.Iodine induced cracking of zircaloy for cladding em adsh a recrview[C].Advances InstrumentationProceedings,1974:275. |
| [23] | LEED;Adamson R B .Zirconium in the nuclear industryASTM STP 633[Z].American Society for Testing and Materials,1977. |
| [24] | usyCC;Tucker R P;McCauley J E .Halogen stress corrosion crackiing of zircaloy-4 tubing[J].Journal of Nuclear Materials,1975,55(01):64. |
| [25] | YaggeeFL;Mattas R F.Effect of zirconium oxide on the stress-corrosion susceptibility of irradiation zircaloy cladding[M].ASTM Special Technical Publication,1982:158. |
| [26] | MillerA;Ocken H .Iodine-induced SCC of zircaloy: laboratory data,a phenomenolgical model, and predictions of inreactor behavior[J].Journal of Nuclear Materials,1981,99(02):254. |
| [27] | 褚武扬.应力腐蚀的位错层次研究[A].北京:化学工业出版社,1999:30. |
| [28] | 黄克智;肖纪美.材料的损伤断裂机理和宏微观力学理论[M].北京:清华大学出版社,1999:230. |
| [29] | KnorrD;Pelloux R M .Effects of material condition on the iodine SCC susceptibility of zircaloy-2 cladding[J].Journal of Nuclear Materials,1982,110(02):230. |
| [30] | 赵文金;周邦新 .Zr-4合金中第二相的研究[J].核动力工程,1991,12(05):67. |
| [31] | KuoT;Wakashima Y et al.Effects of crystallographic orientation on plastic deformation and SCC initiation of zirconium alloys[J].Journal of Nuclear Materials,1985,132(01):126. |
| [32] | FregoneseM;Delette G;Ducros G .Amount of iodine responsible for I-SCC OF Zircaloy-4 in PCI-conditions :recoilimplanted and thermally released iodine[J].Nuclear Engineering and Design,1998,186(12):307. |
| [33] | 扎依莫夫斯基AC;尼古琳娜A B;列晓尼可夫H T;姚敏智.核动力用锆合金[M].北京:原子能出版社,1988:292. |
| [34] | 彭倩,李卫军,唐正华,崔旭梅,衡雪梅.Zr-Sn-Nb合金I-SCC腐蚀产物研究[J].核动力工程,2003(04):312-316. |
| [35] | 李中奎,刘建章,周廉,李聪,赵文金,张建军.新锆合金耐蚀性能研究[J].原子能科学技术,2003(z1):84-87,110. |
| [36] | YuK;Medvedev A V;Nesterov B I .Infuence of irradiation on KISCC of Zr±1%Nb claddings[J].Journal of Nuclear Materials,2000,280(07):106. |
| [37] | VladimirVL;Leonid V M .The evelopment of the crack growth model in zirconium claddings in iodine environment[J].Nuclear Engineering and Design,2002,213(04):133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%