采用酸碱处理的方法对聚酰亚胺(PI)薄膜表面改性.利用万能试验机和热失重仪考察了处理前后PI薄膜力学性能和热性能的变化情况,并通过傅立叶红外光谱仪、原子力显微镜及视频接触角仪对PI薄膜改性前后表面性能进行了表征.结果表明,经酸碱处理后,PI薄膜表面化学组成和表面形貌均发生变化,表面亲水性增大;当处理时间为4 min时,力学性能保持在97%以上,热稳定性略有下降;均方根粗糙度从1.057 nm增大到3.002 nm,接触角从77.32°下降到46.70°,粘接功提高了38.20%.
参考文献
| [1] | 张雯,张露,李家利,张凯.国外聚酰亚胺薄膜概况及其应用进展[J].绝缘材料,2001(02):21-23. |
| [2] | Soo-Jin Park;Eun-Jung Lee;Soo-Han Kwon .Influence of Surface Treatment of Polyimide Film on Adhesion Enhancement between Polyimide and Metal Films[J].Bulletin of the Korean Chemical Society,2007(2):188-192. |
| [3] | Xu Dong Huang;Sunil Madhukar Bhangale;Peter M Moran;Nikolai L Yakovlev;Jisheng Pan .Surface modification studies of Kapton HN polyimide films[J].Polymer international,2003(7):1064-1069. |
| [4] | 王云起,焦延鹏,蔡继业,周长忍.聚乳酸表面处理的AFM观察及对细胞粘附性的影响[J].高分子材料科学与工程,2005(06):181-184,188. |
| [5] | Kim SH.;Lee DW.;Chung KH.;Park JK.;Jaung JY.;Jeong SH. .Improvement in the adhesion of polyimide/epoxy joints using various curing agents[J].Journal of Applied Polymer Science,2002(4):812-820. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%