利用感应区熔法制备了Al2O3/MgAl2O4/ZrO2共晶陶瓷.当坩埚壁温为2200℃、行走速度为2mm/h时,制备了φ10 mm ×62 mm表面光滑致密的陶瓷样品.扫描电镜微观组织图显示Al2O3相和MgAl2O4相为基体相,ZrO2相以棒状镶嵌在基体中.定向凝固共晶陶瓷硬度和断裂韧性达到12 GPa和6.1 MPa·m1/2,为预烧结体的2倍和1.7倍.气孔和晶界的消失及细小规整ZrO2相在基体中的弥散分布,有效提高了材料的硬度和断裂韧性.
参考文献
| [1] | Javier LLorca;Victor M. Orera .Directionally solidified eutectic ceramic oxides[J].Progress in materials science,2006(6):711-809. |
| [2] | A. Otsuka;Y. Waku;R. Tanaka .Corrosion of a unidirectionally solidified Al_2O_3/YAG eutectic composite in a combustion environment[J].Journal of the European Ceramic Society,2005(8):1269-1274. |
| [3] | C. Baudin;A. Sayir;M.H. Berger .Mechanical behaviour of directionally solidified alumina/aluminium titanate ceramics[J].Acta materialia,2006(14):3835-3841. |
| [4] | Su HJ;Zhang J;Cui CJ;Liu L;Fu HZ .Rapid solidification of Al2O3/Y3Al5O12/ZrO2 eutectic in situ composites by laser zone remelting[J].Journal of Crystal Growth,2007(2):448-456. |
| [5] | 苏海军,张军,王常帅,刘林,傅恒志.激光区熔定向凝固Al2O3/YAG/ZrO2共晶自生复合陶瓷的显微组织与断裂韧性[J].北京科技大学学报,2007(02):205-210. |
| [6] | 吴江,张龙,赵忠民,潘传增,张靖,吴铮.微拉法制备氧化物共晶复相陶瓷的研究进展[J].科学技术与工程,2007(04):589-593. |
| [7] | Jong Ho Lee;Akira Yoshikawa;Tsuguo Fukuda .Growth and characterization of Al_2O_3/Y_3Al_5O_12/ZrO_2 ternary eutectic fibers[J].Journal of Crystal Growth,2001(1/2):115-120. |
| [8] | 朱浩,赵忠民,张龙,宋亚林,潘传增.超重力下燃烧合成Al2 O3/ZrO2的成分、结构与性能[J].特种铸造及有色合金,2009(05):455-458. |
| [9] | 苏海军,张军,刘林,傅恒志.激光快速熔凝Al2O3/YAG共晶陶瓷的制备与组织[J].北京航空航天大学学报,2007(07):846-850. |
| [10] | 王珮,孙海滨,白佳海,刘俊成.Al2O3/MgAl2O4共晶陶瓷定向凝固过程固液界面形貌的研究[J].人工晶体学报,2011(05):1252-1257. |
| [11] | 邓杨芳,张军,苏海军,宋衎,刘林,傅恒志.激光区熔Al2O3/Er3Al5O12共晶自生复合陶瓷的组织与断裂韧性[J].无机材料学报,2011(08):841-846. |
| [12] | 王俊涛,陈松林,袁林,赵洪亮,曾鲁举,刘锡俊,陈雪峰.ZrO2对刚玉-尖晶石浇注料抗热震性能的影响[J].硅酸盐学报,2011(08):1317-1322. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%