为研究热效应对铁磷酸玻璃结构的影响,对40Fe2O3-60P2O5玻璃样品在600～800℃进行热处理,获得了结晶样品.利用XRD、Raman等研究了玻璃结晶化过程中的结构变化,指认了铁磷酸盐玻璃微结构的振动模式的归属.结果表明,在600℃,铁磷酸盐玻璃析出的结晶相主要为:Fe(PO3)3和Fe4(P2O7)3,在700℃、800℃玻璃析出的结晶相主要为Fe4(P2O7)3.利用SEM观察了玻璃样品的微观形貌,结晶相的微观形貌为片状,保温时间延长,片层厚度增加.
参考文献
| [1] | Day DE.;Ray CS.;Hrma P.;Wu Z. .Chemically durable iron phosphate glass wasteforms[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):1-12. |
| [2] | 黄文旵,周萘,Day Delbert E,Ray Chandra S.Cr2O3对高放核废料磷酸盐玻璃固化体的影响[J].无机材料学报,2005(04):842-850. |
| [3] | Kim CW.;Day DE. .Immobilization of Hanford LAW in iron phosphate glasses[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2003(1/3):20-31. |
| [4] | 梁晓峰,赖元明,李海建,王翠玲.氧化钠对铁磷酸盐玻璃微结构影响的振动光谱分析[J].硅酸盐通报,2014(03):600-604. |
| [5] | 马微微,肖汉宁.Y2O3掺杂对Al2O3-SiO2-P2O5系统玻璃结构和析晶性能的影响[J].中国陶瓷,2008(06):19-22. |
| [6] | 蒋晓曙,隋普辉,陆雷.热处理制度对LZAS玻璃陶瓷析晶和显微结构的影响[J].硅酸盐通报,2009(04):779-783. |
| [7] | Mogus-Milankovic A;Santic A;Reis ST;Furic K;Day DE .Mixed ion-polaron transport in Na2O-PbO-Fe2O3-P2O5 glasses[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2004(1/3):97-109. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%