利用花岗岩渣粉为硅质原料制备蒸压加气混凝土,以抗压强度为表征指标,通过单因素变量试验讨论了各种配料对制品性能的影响,正交试验确定了原料的最佳配合比,探讨了蒸压养护制度与性能的关系.结果表明,配料对制品性能的影响程度依次为水料比、生石灰、水泥和石膏,蒸压温度和时间决定着水化硅酸钙的产率及结晶度,各因素之间互相协调、制约,合理的配合比和蒸压制度是形成良好孔结构和性能的关键因素.实验条件下,按水料比为0.60,石渣粉:生石灰:水泥:石膏=66∶ 19∶10∶5,铝粉膏0.13％配料,1.2 MPa(188℃)下恒压7h,得到体密度493.8 kg/m3、抗压强度4.4 MPa、导热系数0.119 W/(m·K)的制品.
参考文献
| [1] | Hu1ya Kus;Thomas Carlsson.Microstructural investigations of naturally and artificially weathered autoclaved aerated concrete[J].Cement and Concrete Research,20039(9):1423-1432. |
| [2] | A.Hauser;U.Eggenberger.Fly ash from cellulose industry as secondary raw material in autoclaved aerated concrete[J].Cement and Concrete Research,19993(3):297-302. |
| [3] | N. Narayanan;K. Ramamurthy.Structure and properties of aerated concrete: a review[J].Cement & concrete composites,20005(5):321-329. |
| [4] | A. Laukaitis;B. Fiks.Acoustical properties of aerated autoclaved concrete[J].Applied acoustics,20063(3):284-296. |
| [5] | 刘士红;龚武红.蒸压砂加气混凝土自保温体系应用与研究[J].新型建筑材料,2007(12):50-52. |
| [6] | 王力军.蒸压轻质砂加气混凝土自保温砌体技术[J].低温建筑技术,2013(07):43-44. |
| [7] | H. Kurama;I. B. Topcu;C. Karakurt.Properties of the autoclaved aerated concrete produced from coal bottom ash[J].Journal of Materials Processing Technology,20092(2):767-773. |
| [8] | 钱嘉伟;倪文;李德忠;黄晓燕.利用低硅铜尾矿生产加气混凝土的试验研究[J].新型建筑材料,2011(3):20-24. |
| [9] | 李方贤;陈友治;龙世宗.用铅锌尾矿生产加气混凝土的试验研究[J].西南交通大学学报,2008(6):810-815. |
| [10] | 刘家弟.石材加工粉末废料生产加气混凝土砌块研究[J].非金属矿,2014(4):50-52. |
| [11] | 桂苗苗;蔡振哲.蒸压加气混凝土性能比较及微观分析[J].武汉理工大学学报,2011(6):31-35. |
| [12] | 蔡振哲.花岗岩石粉在加气混凝土中的应用研究[J].墙材革新与建筑节能,2015(06):32-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%