The creep crack growth(CCG)and the time to carck initiation and rupture of specimen (t_(rc)and t_r)were measured by means of electrical potential method on single edge notched specimens at 700℃.The field near the crack tip under steady-state creep was represented by energy rate integral(C~*),and the CCG rate as a function of C~* has been obtained.The agreement between the predicted and observed t_(rc)values is quite good.It was found that the addition of small amount of Mg and Zr in the alloys causes t_(rc)and t_r of the specimens to in- crease significantly.