制备了两种不同玻璃化温度的磷酸盐玻璃（P—glass），研究了P—glass对聚丙烯（PP）基体结晶行为和力学性能的影响。结果表明，P—glass在PP中具有异相成核作用，使PP的结晶温度升高。具有较低玻璃化温度（176℃）的P—glass，能诱导生成口晶，使p-glass／PP复合材料的断裂伸长率与纯PP相比从427％提高至545％，而冲击强度则由18．6kJ／m2提高至36．8kJ／m2，材料的韧性得以显著改善。
Phosphate glass （P-glass）/polypropylene （PP） composites were prepared. The effects of P-glass with different glass transition temperature （Tg） on the crystalline and mechanical properties of PP matrix were studied. The experimental results show that the crystallization temperature of the PP matrix was markedly increased by adding P-glass, in which P-glass with low-rig plays a crucial role in the heterogeneous nucleation process of PP. The addition of low- Tg P- glass leads to the formation of 13 crystals and obvious improvement in toughness. The elongation at break of the composites increases from 427% to 545%, and the impact strength increases from 18.6 kJ/m2 to 36.8 kJ/m2.
参考文献
| [1] | Chen Y, Li H. Effect of ultrasound on the morphology and properties of polypropylene/inorganic filler composites [J]. Journal of Applied Polymer, 2005, 97(4): 1553-1560. |
| [2] | Liang J Z, Li R K Y. Effect of filler content and surface treatment on the tensile properties of glass-bead-filled polypropylene composites [J]. Polymer International, 2000, 49(2): 170-174. |
| [3] | Prashantha K, Soulestin J, Lacrampe M F, et al. Masterbatch-based multi-walled carbon nanotube filled polypropylene nanocomposites: Assessment of rheological and mechanical properties [J]. Composites Science and Technology, 2009, 69(11/12): 1756-1763. |
| [4] | 杨 波, 陈光顺, 李 姜, 等. 多壁碳纳米管增强炭黑/聚丙烯导电复合材料导电行为 [J]. 复合材料学报, 2009, 26(4): 41-46. |
| [5] | Urman K, Otaigbe J U. New phosphate glass/polymer hybrids—Current status and future prospects [J]. Progress in Polymer Science, 2007, 32(12): 1462-1498. |
| [6] | Richard K B. Review: The structure of simple phosphate glasses [J]. Journal of Non-Crystalline Solids, 2000, 263/264: 1-28. |
| [7] | Gupta M, Lin Y, Deans T, et al. Biaxially oriented poly(propylene-g-maleic anhydride)/phosphate glass composite films for high gas barrier applications [J]. Polymer, 2009,50(2): 598-604. |
| [8] | Urman K, Schweizer T, Otaigbe J U. Uniaxial elongational flow effects and morphology development in LDPE/phosphate glass hybrids [J]. Rheologica Acta, 2007, 46(7): 989-1001. |
| [9] | Trotignon J P, Verdu J. Skin-core structure-fatigue behavior relationships for injection-molded parts of polypropylene Ⅰ: Influence of molecular weight and injection conditions on the morphology [J]. Journal of Applied Polymer Science, 1987, 34(1): 1-18. |
| [10] | Shangguan Y, Song Y, Peng M, et al. Formation of β-crystal from nonisothermal crystallization of compression-molded isotactic polypropylene melt [J]. European Polymer Journal, 2005, 41(8): 1766-1771. |
| [11] | Karger-Kocsis J, Varga J. Effects of β-α transformation on the static and dynamic tensile behavior of isotactic polypropylene [J]. Journal of Applied Polymer Science, 1996, 62(2): 291-300. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%