采用乳液聚合法制备粒径为229nm的单分散聚苯乙烯（PS）微球,以单分散PS微球和粒径为10nm的硅溶胶为原料,采用蒸发自组装法在气-液界面上二元共沉积,制备了大孔SiO2材料。结果表明,当SiO2体积分数为11%时,大孔SiO2材料呈现有序规整的FCC结构,其填充率为42%,收缩率仅为2%。低温N2吸附表明该材料在大孔孔壁上存在6.4nm左右的介孔,是一种具有大孔/介孔复合孔道结构的功能材料。
Monodisperse polystyrene microspheres with the size of 229nm were synthesized by emulsion polymerization technique.We have fabricated three-dimensional ordered macroporous silica with silica sol and PS microspheres by using solvent evaporation method.Scanning electron micrographs（SEM） showed that when the silica volume fraction was 11% the best ordered 3DOM silica macroporous material was fabricated.It had regular close-packed face-centered cubic（fcc） structure.The diameter of macroporores was 219nm corresponding to a shrinkage of 4.3%.The fill rate of this material is 42%.The walls of pores contained the mesoporous structure with a narrow pore size distribution in 6.4nm according to the result of N2 adsorption-desorption.
参考文献
| [1] | 董慧媛,刘楣,吴宗汉,汪静,王振林.由介质球构成的三维光子晶体能带结构的平面波研究[J].物理学报,2005(07):3194-3199. |
| [2] | Thakuria H;Borah BM;Das G .Macroporous metal oxides as an efficient heterogeneous catalyst for various organic transformations - A comparative study[J].Journal of molecular catalysis, A. Chemical,2007(1/2):1-10. |
| [3] | Izquierdo Barba I;Martinez A;Doadrio AL;Perez Pariente J;Vallet Regi M .Release evaluation of drugs from ordered three-dimensional silica structures.[J].European journal of pharmaceutical sciences,2005(5):365-373. |
| [4] | Miguez H.;Lopez C.;Mifsud A.;Moya JS.;Vazquez L.;Meseguer F. .EVIDENCE OF FCC CRYSTALLIZATION OF SIO2 NANOSPHERES[J].Langmuir: The ACS Journal of Surfaces and Colloids,1997(23):6009-6011. |
| [5] | 王晓冬,董鹏,仪桂云.制备高质量聚苯乙烯微球胶粒晶体的蒸发自组装法[J].物理学报,2006(04):2092-2098. |
| [6] | 张琦,孟庆波,程丙英,张道中.大直径聚苯乙烯小球自组织方法制备高质量opal晶体[J].物理学报,2004(01):58-61. |
| [7] | Blanco A.;Chomski E.;Grabtchak S.;Ibisate M.;John S.;Leonard SW. .Large-scale synthesis of a silicon photonic crystal with a completethree-dimensional bandgap near 1.5 micrometres[J].Nature,2000(6785):437-440. |
| [8] | Li Yao;Xin Wuhong;Zhao Jiupeng .Fabrication and characterization of three-dimensionally ordered macroporous niobium oxide[J].Solid state sciences,2009(9):1625-1630. |
| [9] | Tessier PM.;Kalambur AT.;Rabolt JF.;Lenhoff AM.;Kaler EW.;Velev OD. .Assembly of gold nanostructured films templated by colloidal crystals and use in surface-enhanced Raman spectroscopy[J].Journal of the American Chemical Society,2000(39):9554-9555. |
| [10] | Subramanian G.;Thorne JD.;Pine DJ.;Manoharan VN. .Ordered macroporous materials by colloidal assembly: A possible route to photonic bandgap materials[J].Advanced Materials,1999(15):1261-1265. |
| [11] | 王晓冬,仪桂云.漂浮法制备SiO2有序大孔材料[J].高等学校化学学报,2007(09):1759-1761. |
| [12] | 王晓冬,仪桂云,董鹏,陈胜利.悬浮液气-液界面二元胶体颗粒的漂浮组装机理[J].物理化学学报,2007(11):1707-1713. |
| [13] | 杨卫亚,郑经堂.胶体晶体模板法制备三维有序排列的大孔SiO2材料[J].化工进展,2006(11):1324-1327. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%