采用锈蚀率测定、腐蚀形貌观察及腐蚀产物分析，研究了钢筋HPB235在0．5％NaCl模拟孔隙液中的腐蚀情况，测试了腐蚀前后钢筋的力学性能变化。结果表明，腐蚀时间从240h延长到720h，钢筋的锈蚀率逐渐增加，腐蚀逐渐加重，但腐蚀产物成分变化不大；腐蚀720h后，钢筋的屈服强度下降不到5％，但抗拉强度和延伸率的下降均超过10％。
The corrosion behavior of reinforcing steel HPB235 in concrete structure in 0. 5% NaCl solution was investigated by corrosion rate measuring, corrosion morphology observation and corrosion scale analysis, and its mechanical properties were tested before and after corrosion. The results showed that the time increased from 240 h to 720 h, the corrosion rate increased and the corrosion became heavier and heavier, but the composition of corrosion scale was not changed obviously. After 720 h, the yield strength decreased by less than 5% , but the tensile strength and the elongation decreased by more than 10%.
参考文献
| [1] | 郭育霞,贡金鑫.盐水条件下不同混凝土中钢筋的快速腐蚀行为的研究[J].腐蚀科学与防护技术,2007(03):218-220. |
| [2] | 鲁照玲.酸性气氛下钢筋混凝土结构腐蚀行为及其机理[J].中国腐蚀与防护学报,2007(02):119-123. |
| [3] | 范颖芳,胡志强,张英姿.受腐蚀钢筋混凝土材料力学性能研究现状[J].四川建筑科学研究,2007(02):59-64. |
| [4] | 李萍,张东晓.混凝土结构中钢筋的腐蚀与防护[J].材料保护,2010(07):44-46. |
| [5] | 阮广雄,刘国荣.钢筋混凝土结构中钢筋腐蚀的治理[J].四川建筑,2006(01):83-86. |
| [6] | 耿欧,李果,袁迎曙.电化学检测技术在混凝土内钢筋腐蚀研究中的应用现状与展望[J].混凝土,2005(02):20-23. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%