为了查明铝针铁矿含量高的红土型铝土矿拜耳法溶出过程中氧化铝溶出率低的原因,研究针铁矿在溶出过程中的转化规律及其对氧化铝溶出率的影响.结果表明:在溶出温度为110~240℃时,该类型铝土矿中的铝针铁矿基本不发生转化,其中的氧化铝难以溶出;提高溶出温度到260℃或在240℃左右溶出时,添加干矿石量3%的石灰可促使铝针铁矿转化为赤铁矿,且氧化铝的溶出率随着针铁矿转化程度的增加而提高.加入非钙质添加剂也可以促使铝针铁矿在溶出过程发生结构转变,且氧化铝几乎完全参与反应,从而说明此类铝土矿中铝针铁矿在溶出过程中难以转变是红土型铝土矿中氧化铝溶出率低的重要原因.
@@@@The transformation law of goethite and its effect on the alumina recovery were investigated in order to determine the reason of low alumina recovery in Bayer digestion process of gibbsitic bauxite with high alumogoethite content. The results show that the goethite present in this kind of bauxite has no obvious change in the digestion temperature range of 110℃to 240℃with low alumina recovery. And alumogoethite can be transformed to hematite by increasing digestion temperature to 260 ℃ or adding lime of 3% of dry ores added at about 240 ℃, and the alumina digestion rate increases with the increase of the goethite conversion degree. Adding non-calcareous additives in the re-digestion process of red mud containing goethite can promote the structure transformation of alumogoethite and thus alumina almost reacts completely. The transition of alumogoethite into other forms in Bayer digestion process is important for alumina recovery for lateritic bauxite.
参考文献
| [1] | 赵恒勤,赵新奋,胡四春,马化龙.我国三水铝石铝土矿的矿物学特征研究[J].矿产保护与利用,2008(06):40-44. |
| [2] | 高建阳,朱军,祝凤美,杨丛林.富铁三水铝土矿中铁矿物的反应特性[J].矿业工程,2008(04):39-41. |
| [3] | Rajko Z. Vracar;S. M. Vukcvevic;Ivana S. Parezanovic .The study of iron chlorination from bauxite for its enrichment[J].Scandinavian Journal of Metallurgy,2001(2):84-90. |
| [4] | Nymphodora Papassiopi;Katerina Vaxevanidou;Ioannis Paspaliaris .Effectiveness of iron reducing bacteria for the removal of iron from bauxite ores[J].Minerals Engineering,2010(1):25-31. |
| [5] | 唐向琪;陈谦德.贵港式三水铝石矿综合利用方案比较[J].轻金属,1995(02):1-6. |
| [6] | LI Xiao-bin,XIAO Wei,LIU Wei,LIU Gui-hua,PENG Zhi-hong,ZHOU Qiu-sheng,QI Tian-gui.Recovery of alumina and ferric oxide from Bayer red mud rich in iron by reduction sintering[J].中国有色金属学报（英文版）,2009(05):1342-1347. |
| [7] | LI Guang-hui;SUN Na;ZENG Jing-hua;ZHU Zhong-pin, JIANG Tao.Reduction roasting and Fe-Al separation of high iron content gibbsite-type bauxite ores[M].Warrendale PA:TMS,2010:14-18. |
| [8] | 梅贤功.广西高铁三水型铝土矿开发利用工艺流程概述[J].轻金属,1993(02):12-17. |
| [9] | 陈世益 .广西铝针铁矿的研究及其意义[J].广西地质,1997,10(02):21-24. |
| [10] | 陈世益;周芳 .广西贵港三水型铝土矿针铁矿中铝的类质同象转换[J].中南矿冶学院学报,1993,24(03):283-288. |
| [11] | J. Murray;L. Kirwan;M. Loan .In-situ synchrotron diffraction study of the hydrothermal transformation of goethite to hematite in sodium aluminate solutions[J].Hydrometallurgy,2009(3/4):239-246. |
| [12] | SUSS A G;MALTZ N S.Aluminium and chromium containing goethites:Composition, properties, behaviour in soda aluminate liquors in presence of silicon, titanium and calcium compounds[M].Warrendale PA:TMS,1991:1343-1347. |
| [13] | MAL’TS N S;MOZZHUKHINA L I.High-temperature leaching of bauxites with a high concentration of aluminogoethite[J].Tsvetnye Metally,1981(11):6-9. |
| [14] | 张志强 .还原烧结高铁含铝物料综合提取铝和铁[D].中南大学,2009. |
| [15] | 刘才群.用红外光谱法研究铝矾土矿物[J].中国陶瓷,1994(01):12-16. |
| [16] | FROST R;RUAN H;KLOPROGGE T .Comparison of the Raman spectra of bayerite,boehmite,diaspore and gibbsite[J].Journal of Raman Spectroscopy,2001,32(09):745-750. |
| [17] | MOHAPATRA M;ROUT K;MOHAPATRA B K;ANAND S .Sorption behavior of Pb(Ⅱ) and Cd(Ⅱ) on iron ore slime and characterization of metal ion loaded sorbent[J].Journal of Hazardous Materials,2009,166(2/3):1506-1513. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%