In this study, reheating of liquidus semi-continuous east billets of 7075 Al alloy wascarried out in a resistance furnace, and the temperature contrast of the outer andthe center of the reheated billets was investigated, then the reheating microstructureswere investigated. Results show that: the difference of temperature between the outerand center is small and the difference of their microstructures are also small. Dur-ing reheating at 576° C the spheroidization of grains is significant after 5rain and norosettes are visible after 20min by optical microscopy. Similar observations were madeon materials reheated at 596° C, but the ripening process is faster. The grains growup to 30-60pm, fine enough for thixoforming.
参考文献
| [1] | D B Spencer;R Mehrabian;M C Flemings .[J].Metallurgical and Materials Transactions,1972(3A):1925. |
| [2] | M C Flemings .[J].Metallurgical and Materials Transactions,1991,22A:957. |
| [3] | M C Flemings.[A].Editmet Spa-Via Corfu102,Turin,Italy,Sept,2000:11. |
| [4] | S B Brown;M C Flemings .[J].Current Advances in Materials and Processes,1993(143):36. |
| [5] | G M Lu;J Z Cui;J Dong;K Xia.[A].Editmet Spa-Via Corfu102,Turin,Italy,2000:701. |
| [6] | Z Q Hu.Metal Solidification[M].北京:冶金工业出版社,1985:59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%