采用固相合成法制备了BiYbO3-PbTiO3-BaTiO3(BYPT-BT)压电陶瓷材料.通过差热分析(DSC)和热失重分析(TG)确定了BYPT-BT陶瓷钙钛矿相的形成温度,研究了不同含量的BaTiO3对BYPT-BT陶瓷相结构及电性能的影响规律.结果表明,BYPT-BT陶瓷由钙钛矿相和焦绿石相Yb2Ti2O7组成,随着BaTiO3含量的增加,焦绿石相Yb2Ti2O7逐渐减少.居里温度丁T和介电损耗tanδ随着BaTiO3含量的增加逐渐减少,介电常数ε,则随之而增大.
参考文献
| [1] | 孙慷;张福学.压电学[M].北京:国防工业出版社,1984 |
| [2] | 陈异,蓝德均,肖定全,朱建国.新型钙钛矿型铁电陶瓷BSPT研究进展[J].材料导报,2005(12):95-98. |
| [3] | Eitel RE;Zhang SJ;Shrout TR;Randall CA;Levin I .Phase diagram of the perovskite system (1-x)BiScO3-xPbTiO(3)[J].Journal of Applied Physics,2004(5):2828-2831. |
| [4] | Richard E.Eitel;Seung-Eek Park;Clive A.Randall;Thomas R.Shrout .PEROVSKETE MATERIAI.S FOR HIGH TEMPERATURE AND HlGH PERFORMANCE ACTUATIORS AND TRANSDUCERS[P].US 668584982,2004-2-3. |
| [5] | Richard E.EITEI;Clive A.RANDAI,I;Thomas R.SHROUT et al.New High Temperature Morphotropic Phase Boundary Piezoelectric Based on Bi(Me)O3-PbTiO3 Ceramics[J].Japanese Journal of Applied Physics,2001,40:5999-6002. |
| [6] | 文海,王晓慧,赵巍,王浩,李龙土,桂治轮.高温压电陶瓷研究进展[J].硅酸盐学报,2006(11):1367-1373. |
| [7] | 李振荣;王晓莉;张良莹 等.铅基弛豫型铁电体钙钛矿结构的稳定性[J].压电与声光,1998,20(02):135-139. |
| [8] | 高峰,张昌松,王卫民,张慧君,田长生.钨掺杂PZN-PZT陶瓷的结构与压电性能的研究[J].材料工程,2005(01):3-7,11. |
| [9] | 王守德,刘福田,程新.PZT掺杂Ba（Cu1/2W1/2）O3的压电陶瓷的性能研究[J].济南大学学报(自然科学版),2004(03):189-191. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%