为研究热轧对7055铝合金淬透性的影响，采用末端淬火实验、硬度测试、光学显微镜和透射电镜研究了不同冷却速率处合金的组织和性能，实验结果表明：合金热轧后淬透性大大降低，淬透深度由约100mm降至约45mm，这主要与慢速淬火时析出的η平衡相的数量和尺寸的改变有关；热轧增加了η平衡相的形核位置，并引入大量的位错，增加了11平衡相的长大速率，因此，热轧合金固溶后慢速淬火时，析出的η平衡相的数量和尺寸都大大增加，时效后形成的η’沉淀强化相数量减少，硬度随冷却速率减小而下降的程度增加，合金的淬透性降低。
To investigate the effect of hot rolling on hardenability of 7055 aluminum alloy, the properties and mierostructure at different cooling rates determined by end-quench method, hardness test, optical microscopy and transmission electron microscopy were studied, and the results showed that the hardenability was decreased significantly after hot rolling with the hardened depth deceasing from about 100 mm to 45 mm. This is because the number and size of η equilibrium phase formed during slow quenching are changed by hot rolling. Hot rolling increases the nucleation sites for η equilibrium phase, and introduces a number of dislocations which prompt growth of η equilibrium phase. As a result, in the hotrolled and solution treated alloy, more η equilibrium phase particles with larger size are formed during slow quenching, which decreases the number of strengthening η precipitates after aging. Thus the drop in the hardness with the decreasing of cooling rate is increased, which decreases the hardenability.
参考文献
| [1] | S.D. Liu;X.M. Zhang;M.A. Chen .Influence of aging on quench sensitivity effect of 7055 aluminum alloy[J].Materials Characterization,2008(1):53-60. |
| [2] | S.T. Lim;S.J. Yun;S.W. Nam .Improved quench sensitivity in modified aluminum alloy 7175 for thick forging applications[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):82-90. |
| [3] | 张勇 .7050铝合金材料淬透性的末端淬火研究[D].中南大学,2008. |
| [4] | Zhang, X.;Liu, W.;Liu, S.;Zhou, M. .Effect of processing parameters on quench sensitivity of an AA7050 sheet[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(3):795-802. |
| [5] | 张勇,邓运来,张新明,刘胜胆,杨柳.7050铝合金热轧板的淬火敏感性[J].中国有色金属学报,2008(10):1788-1794. |
| [6] | 熊柏青,李锡武,张永安,李志辉,朱宝宏,王锋,刘红伟.新型高强韧低淬火敏感性Al-7.5Zn-1.65Mg-1.4Cu-0.12Zr合金[J].中国有色金属学报,2009(09):1539-1547. |
| [7] | 伊琳娜,汝继刚.7B04铝合金锻件淬透性的研究[J].航空材料学报,2003(z1):288-288. |
| [8] | J. D. Robson;P. B. Prangnell .Predicting recrystallized volume fraction in aluminium alloy 7050 hot rolled plate[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(6):607-614. |
| [9] | Robson JD. .Optimizing the homogenization of zirconium containing commercial aluminium alloys using a novel process model[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):219-229. |
| [10] | 李劲风,郑子樵,任文达.第二相在铝合金局部腐蚀中的作用机制[J].材料导报,2005(02):81-83,90. |
| [11] | 尹志民,方家芳,黄继武,聂波,单长智,郭加林,王琳.时效工艺对7A52铝合金晶间腐蚀和剥蚀行为的影响[J].中南大学学报（自然科学版）,2007(04):617-622. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%