本文采用真空蒸发制备了V2O5薄膜，用电化学方法从Li离子电解质中向V2O5薄膜注入Li离子.研究了V2O5薄膜中Li离于储存特性、注入／退出可逆性以及电荷注入对其光学性能的影响．实验结果表明，V2O5薄膜具有较好的Li离子储存特性和注入／退出可逆性，Li离子的注入量受到膜中V5+的含量以及锂离子可占据的总位置数限制，而且离子注入后V2O5薄膜的光学性能变化较小．
Lithium was inserted electrochemically from an electrolyte into V2O5 thin films prepared by evaporation and posttreated at different temperatures in air
so that LixV2O5 was obtained. Li+ storage properties, reversibiliy of Li+ intercalation/deintercalation in V2O5 thin films and influence of
Li+ insertion on their optical properties were investigated. The experimental results show that two factors, the V5+ concentration and the sum total of
sites in V2O5 thin films, control the capacity of Li+ insertion into V2O5 thin films, and that these thin films have a good Li+ storage characteristic,
stability and reversibility.
参考文献
| [1] | Whittingham M S. Pro. Solid State Chem., 1978, 12: 41. 2 Maier J. In Science and Technology of Fast Ion Conductors, Vol. 199, eds. Tuller H L and Balkanski M, (Plenum Press, New York, 1989) P. 299. 3 吴广明, 吴永刚等. 材料科学与工程, 1996, 14 (3): 11. 4 Soud A M A E, Mansour B, Soliman L I. Thin Solid Films, 1994, 247: 140. 5 Pecquenard B, Gourier D, Baffier N. Solid State Ionics, 1995, 78: 287. 6 吴广明, 吴永刚等. 应用科学学报, 1997, 15 (3): 44. 7 Fujita Y, Miyazaki K, Tatsuyama C, Japn. J. Appl. Phys., 1985, 24 (8): 1082. 8 Shimizu Y, Nagase K, Miura N, et al. Solid State Ionics, 1992, 53--56: 490. 9 Murawski L, Gledel C, Sanchez C, et al. J. Non-Cryst. Solids, 1989, 89: 98. 10 Andersson A M, Granqvist C, Stevens J R. Applied Optics, 1989, 28 (15): 3295. 11 West K, Zachan-Christiansen B, Jacobsen T, et al. Solid State Ionics, 1995, 76: 15. 12 Baffier N, Zmaidi L, Huber M. Mat. Res. Bull., 1990. 705. 13 Schlotter P. Solar Energy Materials, 1987, 16: 39. 14 吴永刚, 吴广明等. 无机材料学报, 1996, 11 (4): 633. 15 Cogan S F, et al. J. Appl. Phys., 1989, 66 (3): 1333. |