通过对合金进行不同温度的固溶处理、蠕变曲线测定及组织形貌观察,研究了热处理工艺对4.5％Re镍基单晶合金中温蠕变行为的影响.结果表明:随着固溶温度提高,可降低元素的偏析程度,提高合金的蠕变性能.在760℃/800MPa条件的蠕变期间,合金中γ’相不形成筏状组织,但在近断口区域,立方γ '相的扭曲程度增加.合金在蠕变期间的变形特征是位错在基体中运动和剪切γ'相,其中,切入γ'相的＜110＞超位错可由｛111｝面交滑移到｛100｝面,形成K-W锁,而切过y’相的＜110＞超位错在｛111｝面发生分解,可形成(1/3)＜112＞超肖可莱不全位错+层错的位错组态,阻碍位错运动和抑制位错的交滑移.
参考文献
| [1] | Mackay R A;Nathal M V;Pearson D D .[J].Metallurgical and Materials Transactions,1990,21:381. |
| [2] | Nystrom J D;Pollck T M;Murphy W H et al.[J].Metallurgical and Materials Transactions,1997,28:2443. |
| [3] | Yeh A C;Tin S .[J].Scripta Materialia,2005,52:519. |
| [4] | Erickson G L.[A].Kyongju,Korea:RICAM,1995:18. |
| [5] | Simonetti M;Caron P .[J].Materials Science and Engineering,1998,A254:1. |
| [6] | Zhao K;Ma Y H;Lou L H et al.[J].Materials Transactions,2005,46(01):54. |
| [7] | Li Jiarong;Tang Dingzhong;Liu Shizhong.[J].Journal of Materials Engineering,1999(02):3. |
| [8] | 马文有,李树索,乔敏,宫声凯,郑运荣,韩雅芳.热处理对镍基单晶高温合金微观组织和高温持久性能的影响[J].中国有色金属学报,2006(06):937-944. |
| [9] | Rüsing J;Wanderka N .[J].Scripta Materialia,2002,46:235. |
| [10] | Yun H M .[J].Materials Science and Engineering,1993,A165:65. |
| [11] | Kearsey R M;Beddoes J C;Jaansalu K M.[A].New York:Metals and Materials Society,2004:801. |
| [12] | 任英磊,金涛,管恒荣,胡壮麒.固溶处理对1种镍基单晶高温合金组织的影响[J].稀有金属材料与工程,2003(04):287-290. |
| [13] | 于兴福,田素贵,王明罡,尚丽娟,崔树森.Ni-Al-Re/Ru合金的层错能[J].材料研究学报,2008(05):515-520. |
| [14] | Hemker K J;Mills M J;Nix W D .[J].Acta Metallurgica Et Materialia,1991,39(08):1901. |
| [15] | Kear B H et al.[J].Transactions of the Metallurgical Society of AIME,1962,224:382. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%