Weathering steel is widely used in various ifelds due to its excellent mechanical properties and high corrosion resistance. The effect of chromium content on the S450EW weathering steel in cyclic immersion test was studied. The results indicated that the corrosion resistance of S450EW weathering steel is closely related to chromium content. The addition of chromium signiif-cantly inhibited the weathering steel corrosion. The corrosion rate of experimental steel after 96 h immersion was 1.101 g·m?2·h?1. The rust of S450EW weathering steel was mainly constituted of FeOOH and Fe3O4 phase, and the elevation of chromium content promoted the formation of α-FeOOH. The ifne precipitates of the two phases contributed to the formation of dense dust layer of test steel. Furthermore, the increase of chromium is beneifcial for the cure of original defects and cracks of the rust layer via the enrich-ment of chromium. The corrosion potential and the resistance of corrosion process were thus increased, protecting the experimental steel from further corrosion. A S450EW steel with corrosion resistance more than 1.5 times of Q450NQR1 steel was prepared.
参考文献
| [1] | Q.C.Zhang;J.S.Wu .[J].Materials Review,2000,14(7):12-13. |
| [2] | Q.Y.Liu;H.Dong;Y.Weng;P.Qu,J.Y.Xu,B.W.Chen .[J].Iron and Steel,2004,39(4):45-48. |
| [3] | P.Dillmann;R.Balasubramaniam;G.Beranger .[J].Corrosion Science,2002,44:2231-2242. |
| [4] | M.Yamashita;H.Miyuki;Y.Matsuda .[J].Corrosion Science,1994,36:283-289. |
| [5] | L.J.Yue;L.M.Wang;X.Y.Piao;C.H.Xu,J.X.Zhu .[J].J Iron Steel Res,2006,18(1):34-38. |
| [6] | Y.S.Choi;J.J.Shim;J.G.Kim .[J].Journal of Alloys and Compounds,2005,391:162-169. |
| [7] | H.R.Hou;J.Y.Fu .[J].Iron and Steel,2004,39(6):71-74. |
| [8] | B.Zhang .[J].China Metallrugy,2005,86(1):4-6. |
| [9] | H.E.Townsend .[J].CORROSION,2001,57:497-501. |
| [10] | Y.H.Qian;Z.G.Li.[J].Baosteel Technology,2007(2):5-8. |
| [11] | F.Izumi;T.Ikeda .[J].Materials Science Forum,2000,321/324:198-204. |
| [12] | S.Hoerlè;F.Mazaudier;P.Dillmann;G.Santarini .[J].Corrosion Science,2004,46:1431-1465. |
| [13] | L.H.Liu;H.B.Qi;Y.P.Lu;H.Z.Han .[J].Corrosion Science and Pro-tection Technology,2003,15(2):86-89. |
| [14] | I.Odnell;C.Leygraf .[J].Corrosion Science,2001,43:2379-2396. |
| [15] | T.Kamimura;S.Nasu;T.Segi .[J].Corrosion Science,2003,45:1863-1879. |
| [16] | T.Sasaki;J.Itoh;Y.Horiguchi .[J].Corrosion Science,2006,48:4339-4351. |
| [17] | T.Kamimura;S.Hara;H.Miyuki;M.Yamashita H.Uchida .[J].Corrosion Science,2006,48:2799-2812. |
| [18] | G.P.Zhou;Z.Y.Liu;Y.Q.Qiu;G.D.Wang .[J].Mater Des,2009,30:4342-4347. |
| [19] | H.L.Jun;C.W.Xiao;Q.L.Jia;W.Z.Cheng,Z.Hui,Y.P.Feng .[J].Iron and Steel,2013,48(2):75-79. |
| [20] | H.Fei;F.Liu;B.X.Wang;C.Y.Wu,Y.B.Liu,F.S.Wang .[J].Transac-tions of Materials and Heat Treatment,2012,33(1):110-116. |
| [21] | H.Konishi;M.Yamashita;H.Uchida;J.Mizuki .[J].Materials Transactions,2005,46:337-341. |
| [22] | Q.C.Zhang;J.S.Wu;J.J.Wang;W.L.Zheng J.G.Chen A.B.Li .[J].Materials Chemistry and Physics,2003,77:603-608. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%