本工作研究了应力比和载荷频率对高强度低碳硅锰钢在蒸馏水及3.5%NaCl溶液中腐蚀疲劳断口形貌的影响。试验结果表明,在介质影响疲劳裂纹扩展行为的范围内的断口上,随着应力比的增加或者载荷频率的减小,应力腐蚀开裂的断口形貌所占比例逐渐增加。根据多视域的观测结果,建立起了腐蚀疲劳断裂机制示意图。

The change of corrosion fatigue(CF) fractography with stress ratio (R) and frequency (f) were studied in distilled water and 3.5% NaCl aqueous solution. It is shown that the variations of CF fractography with increase in R or decrease in f are similar, i. e., the tendency of stress corrosion cracking (SCC)fractography increased with increase in R or decrease in f on CF fractography. A mechanism schetch map of crack propagation which indicated the influence of R and f on CF cracking mechanism was presented.