由于高岭土中含铁杂质的存在,很大程度上影响了其煅烧产物的白度和色调,而现有技术很难经济地将含铁杂质除尽,因而使高岭土的应用受到很大限制.选择铁含量较低的山西煤系高岭土,研究了化学沉积法实现煤系高岭土表面载钴,并经过煅烧,改善煅烧产物色度指标.研究表明,与未处理样品比较,载钴处理后的样品煅烧产物白度值可提高2～5度,并能调整色调a*、b*值由正值(红黄色)到负值(蓝绿色)；针对实验样品,钴盐添加量的适宜添加比例为煤系高岭土质量的1/500～1/700.
参考文献
| [1] | Chandrasekhar S;Ramaswamy S .[J].Applied Clay Science,2006,33(3-4):269-277. |
| [2] | F. Larroyd;C.O. Petter;C.H. Sampaio .Purification of north Brazilian kaolin by selective flocculation[J].Minerals Engineering,2002(12):1191-1192. |
| [3] | Chandrasekhar S;RamaswamyS .[J].Applied Clay Science,2002,21(3-4):133-142. |
| [4] | 侯太鹏.高岭土除铁、增白试验研究[J].非金属矿,2001(04):32-35,10. |
| [5] | Raghavan P;Chandrasekhar S;Damodaran A D .[J].International Journal of Mineral Processing,1997,50(04):307-316. |
| [6] | 高玉娟,闫平科,王万起,马正先.阜新高岭土化学除铁增白研究[J].中国非金属矿工业导刊,2010(03):31-32,45. |
| [7] | Murray Haydn H;Elzea Kogel J .[J].Applied Clay Science,2005,29(3-4):199-206. |
| [8] | 郑水林,李杨,许霞.温度对煤系煅烧高岭土物化性能影响的研究[J].硅酸盐学报,2003(04):417-420. |
| [9] | González J A;del C Ruiz M .[J].Applied Clay Science,2006,33(3-4):219-229. |
| [10] | 吴基球,简秀梅,李红敏,李竟先.高岭土除铁增白技术的研究[J].中国陶瓷,2006(02):46-48. |
| [11] | 杨晓杰,陈开惠.高岭土精矿中微量微细粒铁、钛赋存状态研究[J].中国粉体技术,2004(z1):132-135. |
| [12] | Cameselle C;Ricart M T;Nú(n)ez M J et al.[J].Hydrometallurgy,2003,68(1-3):97-105. |
| [13] | Ambikadevi V R;Lalithambika M .[J].Applied Clay Science,2000,16(3-4):133-145. |
| [14] | Zhangzhun Lu;Min Ren;Hengbo Yin .Preparation of nanosized anatase TiO2-coated kaolin composites and their pigmentary properties[J].Powder Technology: An International Journal on the Science and Technology of Wet and Dry Particulate Systems,2009(2):122-125. |
| [15] | 陈洁渝,严春杰,韩利雄,涂兵田.煅烧高岭土表面包覆二氧化钛实验研究[J].非金属矿,2008(06):38-40. |
| [16] | 丁希楼,张国栋.高岭土颗粒表面包覆二氧化钛膜的工艺研究[J].矿业研究与开发,2004(01):34-36. |
| [17] | 黄明雯,宋鹂,张金朝.草酸钴对钴蓝颜料性能的影响[J].华东理工大学学报(自然科学版),2008(04):533-536. |
| [18] | 张翊.CIE 1976（L*a*b*）色空间在PVC-U型材颜色测量中的应用[J].聚氯乙烯,2007(05):32-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%