重点研究了多晶硅扩散氧化层对电池性能的影响,并对大规模生产多晶硅扩散工艺进行了优化研究.采用少子寿命测试仪分析了扩散前后的硅片少子寿命,发现当扩散氧化时的干氧流量控制在2800sccm,扩散后的方块电阻控制在60～70Ω/□时,扩散后硅片少子寿命最高达到了10.45μs,与扩散前的硅片少子寿命相比延长了5倍多;此时的太阳电池并联电阻和短路电流分别高达40.4Q和8522mA,光电转换效率也由16.69％(干氧流量2000sccm)提高到了16.83％.此外,主要针对扩散氧化层对片内方阻均匀性及少子寿命的影响做了解释.
参考文献
| [1] | 邓韡,陈长缨,洪岳,傅倩.量值恒定的表面光电压法测量半导体少子扩散长度的研究[J].半导体光电,2010(05):751-753. |
| [2] | A. A. Istratov;T. Buonassisi;R. J. McDonald;A. R. Smith;R. Schindler;J. A. Rand;J. P. Kalejs;E. R. Weber .Metal content of multicrystalline silicon for solar cells and its impact on minority carrier diffusion length[J].Journal of Applied Physics,2003(10):6552-6559. |
| [3] | Higgs V;Lightowlers E C;Norman C E.Characterisation of dislocations in the presence of transition metal contamination[A].Lehigh University,USA,1992:1309. |
| [4] | McHugo SA;Hieslmair H;Weber ER .Gettering of metallic impurities in photovoltaic silicon[J].Applied physics, A. Materials science & processing,1997(2):127-137. |
| [5] | Narayanan S;Wenham S R;Green M A .High efficiency polycrystalline silicon solar cells using phosphorus pretreatment[J].Applied Physics Letters,1986,48(13):873. |
| [6] | Loghmarti M;Stuck R;Muller J C et al.Strong improvement of diffusion length by phosphorus and aluminum gettering[J].Applied Physics Letters,1993,62(09):979. |
| [7] | 唐骏,黄笑容,席珍强,杜平凡,姚剑,徐敏.铸造多晶硅硅片的磷吸杂研究[J].能源工程,2007(03):34-36. |
| [8] | 陈金学,席珍强,吴冬冬,杨德仁.变温磷吸杂对多晶硅性能的影响[J].太阳能学报,2007(02):160-164. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%