Ce0.6Zr0.3RE0.1O2(RE=Y, La, Pr, Tb)solid solutions were prepared by co-precipitation technique and characterized by a series of methods. XRD and FT-Raman results show that Ce0.6Zr0.3RE0.1O2 has cubic fluorite structure. The different dopant ion radii bring different effect on the cell parameter of Ce0.6Zr0.3RE0.1O2. The X-ray photoelectron spectroscopy (XPS) results show that the binding energy of Ce3d, Zr3d and O1s for Ce0.6Zr0.3RE0.1O2 rises compared with that for Ce0.6Zr0.4O2, indicating that dopant elements change chemistry environment of solid solutions which is available to improve redox performance. Compared with Pd/Ce0.6Zr0.4O2, doping Y and La does not change air/fuel (A/F) characteristic of TWCs, but doping Pr and Tb widens A/F operating window and makes HC, CO and NO have higher conversion. The light-off temperature of Pd/Ce0.6Zr0.3La0.1O2 is corresponding to that of Pd/Ce0.6Zr0.4O2. However, the light-off temperatures of Pd/Ce0.6Zr0.3M0.1O2 (M=Y, Pr, Tb) are lower than that of Pd/Ce0.6Zr0.4O2, which keep much lower after high temperature treatments. Among Pd/Ce0.6Zr0.3RE0.1O2, Pd/Ce0.6Zr0.3Tb0.1O2 represents wider A/F operating window, higher conversion, lower light-off temperature and better high-temperature resistance.
参考文献
| [1] | Trovarelli A .Catalytic properties of ceria and CeO2-containing materials[J].Catalysis Reviews-science and Engineering,1996,38(04):439. |
| [2] | Di Monte R;Fornasiero P;Kaspar J et al.Stabilisation of nanostructured CeO2-ZrO2 solid solutions by addition of storage/release promoters for three-way catalysts[J].Studies In Surface Science and Catalysis,2001,140:229. |
| [3] | Colon G;Pijolat M;Valdivieo F et al.Surface and structural characterization of CexZr1-xO2 CEZIRENCAT mixed oxides as potential three-way catalyst promoters[J].JOURNAL OF THE CHEMICAL SOCIETY FARADAY TRANSACTIO,1998,94(24):3717. |
| [4] | Liotta L F;Macalusa A;Longo A.Effects of redox treatments on the structural composition of ceria-zirconia oxide for application in the three-way catalysis[J].Applied Catalysis A:General,2002(01) |
| [5] | 胡玉才.铈锆氧化物固溶体的制备、表征及三效催化性能[J].材料科学与工艺,2005(01):34-37. |
| [6] | 纳米Ce0.8Zr0.2O2固溶体的溶剂热制备与催化性能研究[J].功能材料,2005(09):1464-1466,1471. |
| [7] | Ikryannikova L N;Aksenov A A;Markaryan G L et al.The red-ox treatments influence on the structure and properties of M2O3-CeO2-ZrO2 (M=Y,La) solid solutions[J].Applied Catalysis A:General,2001,210:225. |
| [8] | Trovarelli A .Structure and oxygen storage/release properties of CeO2-based solid solutions[J].Comments on Inorganic Chemistry,1999,20(4-6):263. |
| [9] | 冯长根,胡玉才,王丽琼.铈锆氧化物固溶体对全钯三效催化剂性能的影响[J].应用化学,2003(02):159-162. |
| [10] | Han Jiancheng.X-ray Diffraction Analyse of Multicrystal[M].上海:华东师范大学出版社,1989 |
| [11] | Trovarelli A.;Rocchini E.;de Leitenburg C.;Dolcetti G.;Boaro M. .Some recent developments in the characterization of ceria-based catalysts[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(0):584-591. |
| [12] | Galtayries A.;Riga J.;Blanchard G.;Caudano R.;Sporken R. .XPS comparative study of ceria/zirconia mixed oxides: powders and thin film characterisation[J].Journal of Electron Spectroscopy and Related Phenomena,1998(0):951-956. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%