在真空气相沉积条件下制备厚度分别为0.32 μm、2.39 μm、7.98 μm和17.11 μm的聚氯代对二甲苯膜(PC膜),采用X射线衍射仪(XRD)、原子力显微镜(AFM)和纳米压痕仪对不同厚度PC膜的结晶度、表面形貌以及力学性能进行了表征与测试.结果表明,随着成膜厚度的增加,聚氯代对二甲苯薄膜的结晶度提高,表面晶粒尺寸增大,结晶形态更加完整,其表面粗糙度、压入模量和压入硬度呈逐渐增大的趋势.而PC膜表面形貌、力学性能的差异又与结晶度密切相关.
参考文献
| [1] | Sean Pursel;Mark W.Horn;Melik C.Demirel;Akhlesh Lakhtakia .Growth of sculptured polymer submicronwire assemblies by vapor deposition[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(23):9544-9548. |
| [2] | Thickness-controlled hydrophobicity of fibrous Parylene-C films[J].Materials Letters,2010(9):p.1063. |
| [3] | Huang Hongliang;Xu Yongan;Hong Yee Low .Effccts of film thickness on moisture sorption,glass transition temperature and morphology of poly(chloro-p-xylylene) film[J].Polymer,2005,46(16):5949. |
| [4] | Jay J. Senkevich;Seshu B. Desu .Morphology of poly(chloro-p-xylylene) CVD thin films[J].Polymer: The International Journal for the Science and Technology of Polymers,1999(21):5751-5759. |
| [5] | 李小龙 .聚氯代对二甲苯薄膜的γ辐照效应研究[D].绵阳:中国工程物理研究院,2006. |
| [6] | 程克梅,何芳,夏云霞,左玉芬.用原子力显微镜观察HMX基炸药老化前后的表面形貌变化[J].含能材料,2005(z1):30-35. |
| [7] | 陈艳平 .聚氯代对二甲苯膜的沉积聚合及退火处理研究[D].绵阳:中国工程物理研究院,2008. |
| [8] | 李河清,蔡殉,陈秋龙.纳米压入技术表征薄膜（涂层）的力学性能[J].材料热处理学报,2001(04):52-55. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%