为了探讨45钢上纳米WC／Ni60B激光熔覆层在磨损过程中出现的相变及析出位置，采用MM-200磨损试验机，将纳米碳化钨增强的Ni基激光熔覆层与硬质合金磨轮进行对磨，采用MX2600FE场发射扫描电镜对熔覆层表／截面组织、磨损后的表／截面组织以及磨屑进行观察分析。结果表明：熔覆层磨损表面和距离磨损区表面约10um的亚表层析出纳米级颗粒，磨屑中也有类似的析出颗粒，析出颗粒的形貌为白色球状，粒径尺寸为数十至数百纳米。
参考文献
| [1] | 周圣丰,曾晓雁,胡乾午,黄永俊.激光-感应复合熔覆Ni基WC复合层的工艺研究[J].激光技术,2009(02):124-126,137. |
| [2] | Martin A.;Fernandez JE.;Vijande R.;Rodriguez J. .Sliding wear behaviour of plasma sprayed WC-NiCrBSi coatings at different temperatures[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(2):1017-1022. |
| [3] | 吴莹,牛焱.激光熔覆添加碳化钨的镍基合金层的组织和硬度研究[J].材料保护,2005(02):61-63. |
| [4] | Hidouci A;Pelletier J M;Ducoin F et al.Micro- structural and mechanical characteristics of laser coatings[J].Sur- face and Coatings Technology,2000,123(01):17-23. |
| [5] | 曾晓雁;吴新伟;陶曾毅 等.激光熔覆Ni-WC金属陶瓷层的耐磨性分析[J].金属学报,1997,33(08):885-890. |
| [6] | Yang Q Q;Senda T;Ohmori A .Effect of carbide grain size on microstructure and sliding wear behavior of HVOF- sprayed WC-12%Co coatings[J].Wear,2003,254(01):23-24. |
| [7] | 张宇,钟敏霖,刘文今.送粉激光熔覆合成制备WC/Ni硬质合金涂层及其耐磨性[J].金属热处理,2005(11):1-5. |
| [8] | 谌俊,肖雪军.激光熔覆纳米WC/Ni60涂层水润滑磨损组织变化特征[J].激光杂志,2011(06):43-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%