分别以粒径为30、70 nm,1、4、7.5 μm的SiC微粒作为增强相制备Ni-SiC复合镀层,并对比研究微粒粒径对复合镀层形貌结构与硬度的影响.结果表明:微粒的引入不同程度影响复合镀层的形貌结构与硬度,致使择优取向由(111)晶面转变为(200)晶面;以纳米微粒作为增强相制备的复合镀层,形貌平整致密,硬度更高,约达520HV,且在(200)晶面呈明显择优取向;较均匀分布的纳米微粒充分发挥弥散强化和细晶强化作用,进而改善复合镀层的形貌结构与性能.
参考文献
| [1] | 谭澄宇 .Ni、Cu基复合镀层制备及其电化学基础研究[D].中南大学,2008. |
| [2] | Vaezi MR;Sadrnezhaad SK;Nikzad L .Electrodeposition of Ni-SiC nano-composite coatings and evaluation of wear and corrosion resistance and electroplating characteristics[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2008(1/3):176-182. |
| [3] | 张本生,王影,张永.铁基纳米氧化铝镀层修复发动机关键部件研究[J].兵器材料科学与工程,2012(03):48-51. |
| [4] | 侯峰岩 .脉冲电沉积Ni-ZrO_2纳米复合镀层的制备、表征及机理研究[D].天津大学,2005. |
| [5] | Borkar, T.;Harimkar, S.P. .Effect of electrodeposition conditions and reinforcement content on microstructure and tribological properties of nickel composite coatings[J].Surface & Coatings Technology,2011(17/18):4124-4134. |
| [6] | Moller, A;Hahn, H .Synthesis and characterization of nanocrystalline Ni/ZrO sub 2 composite coatings[J].Nanostructured Materials,1999(1/4):259-262. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%