用电弧放电法在H2+CH4+Ar的混合气氛中蒸发Fe-Ti合金制备了Fe-TiC复合纳米粉体.用XRD、TEM、DSC-TG、化学分析和氧含量分析等手段对样品进行了分析.结果表明,粉体由Fe、TiC和少量Fe3C组成,复合粒子的形态主要有哑铃形和多面体形,复合粒子的生成机制遵寻VLS机制.在室温大气条件下,粉体中TiC相的含量越高则抗氧化性越好.在流动空气中,温度高于330℃时样品氧化明显加快,在410℃左右,TiC纳米粒子氧化分解.
参考文献
| [1] | 邹光正.TiC/Fe复合材料的自蔓延高温合成工艺及应用[M].北京:冶金工业出版社,2002 |
| [2] | Dogan O N;Hawk J A .[J].Scripta Metallurgica Material,1995,33(06):953-958. |
| [3] | Said A;Chrysanthou A;Wood J V .[J].Journal of Materials Science,1994,29(21):4993-4998. |
| [4] | 邹正光,傅正义,袁润章.自蔓延高温合成TiC复合添加剂增强铁基粉末冶金材料[J].中国有色金属学报,2001(03):408-411. |
| [5] | Licheri R;Orru R;Cao G et al.[J].Ceramics International,2003,29:519-526. |
| [6] | Zhang Weifang;Zhang Xinghong;Wang Jianli et al.[J].Materials Science and Engineering A,2004,381:92-97. |
| [7] | Wang Yisan;Zhang Xinyuan;Zeng Guangting et al.[J].Composites Part A:Applied Science and Manufacturing,2001,32:281-286. |
| [8] | Singh A;Porter WD;Dahotre NB .Thermal transitions in Fe-Ti-Cr-C quaternary system used as precursor during laser in situ carbide coating[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):318-325. |
| [9] | 宋延沛,毛协民,董企铭,周国锋,欧阳志英.WC颗粒增强铁基复合材料的性能研究[J].功能材料,2005(10):1517-1520. |
| [10] | 吴军;王成国;孙康宁 .[J].金属热处理学报,1996,17(04):47-51. |
| [11] | 王成国;吴军;刘玉先 等.[J].粉末冶金技术,1998,16(01):52-56. |
| [12] | 李志杰,潘学铃,孙维民,曲家惠,王福.Al3O3N纳米线的制备与表征[J].物理学报,2005(01):450-453. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%