Phase analysis for the coated surface with B4C and Y2O3 of cemented carbid e WC-20Co in vacuum-heating was carried out by high-temperature X-ray diffra ction from ambient temperature to 1300 ℃. The results show that, the high-conc entration active boron atoms are released from the boron-supply agent B4C loc ated on the alloy surface and diffused into the γ-phase, leading to forming th e three-element boron-bearing compound W2Co21B6 beside forming boron -bearing compounds on the blank surface. By contrast with boronising only, the element yttrium in boronization broadens the boronising temperature range during vacuum-sintering, catalyzes the decarbonisation decomposition of B4C and prom otes diffusion of active boron atoms into the bulk of WC-Co.
参考文献
| [1] | Zhuzhou Cemented Carbides Works.Production of Cemented Carbid es(in Chin.)[M].北京:冶金工业出版社,1974:462. |
| [2] | Xiao Yulin.Case boronization of hard metal cemented by steel[J].Cemented Carbides(in Chin),1981(02):20. |
| [3] | Zhang Hongzhe;Huang Hui.The boronization and La-boronization of cem ented carbides die[J].Cemented Carbides(in Chin),1990(01):49. |
| [4] | Dowson A G;Bernard W;Amande W .Boron addition lowers sintering tempe rature in WC-Co alloys[J].Metal Powder Report,1987,42(12):879. |
| [5] | Tangnade Xi Pengningdun .用硼处理过的硬质合金[P].CN 1038120A,1998. |
| [6] | 刘寿荣,梁福起,孙景,郝建民.WC-8Co硬质合金中稀土添加剂的作用[J].中国稀土学报,1998(01):45-49. |
| [7] | Zou Xumei.Study on change course of microstructure in WC-Co alloy[J].Cemented Carbides(in Chin),1988(04):55. |
| [8] | Lu Yuanming;Zhang Chaofan;Peng Rideng.Overseas Cemented Carb ides (in Chin.)[M].北京:冶金工业出版社,1976:483. |
| [9] | Liu Shourong;Liu Yi .β→α transformation of γ-phasein WC- Co cemented carbides[J].Journal of Materials Science and Technology,1996,12(05):398. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%