采用磁控溅射法交替溅射WS2和石墨靶制备周期为4～23 nm的WSx/a-C纳米多层膜.采用扫描电镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)和X射线光电子谱(xPs)等分析薄膜的组织结构和元素的化学价态;采用纳米压痕仪、涂层附着力划痕仪和球盘式摩擦磨损试验机测试薄膜的硬度、结合力和在潮湿大气下(相对湿度70％)的摩擦磨损特性.结果表明:多层膜结构致密,表面平整.a-C的加入改变WS2的结晶状态,多层膜为微晶或非晶结构;随着调制周期的增大,多层膜的硫与钨摩尔比逐渐降低并趋于稳定(约为1.32),其硬度稍有上升,而结合力明显降低,摩擦因数由0.32降至0.26,而磨损率逐渐上升但显著低于纯WSx膜的.调制周期为4nm的多层膜的耐磨性能最佳,磨损率约为1.03×10-13 m3.N-1.m-1.
参考文献
| [1] | 邢鹏飞;柳卓;由继龙;海力;翟玉春.WS2微粉的物理性能及热稳定性[J].中国有色金属学报,1999(04):811-814. |
| [2] | 王新平;肖金坤;张雷;周科朝.银合金粉末粒度对Ag-MoS2复合材料摩擦磨损性能的影响[J].中国有色金属学报,2012(10):2811-2817. |
| [3] | T.W. Scharf;A. Rajendran;R. Banerjee;F. Sequeda.Growth, structure and friction behavior of titanium doped tungsten disulphide (Ti-WS_2) nanocomposite thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,200919(19):5666-5675. |
| [4] | Deepthi, B.;Barshilia, H.C.;Rajam, K.S.;Konchady, M.S.;Pai, D.M.;Sankar, J.;Kvit, A.V..Structure, morphology and chemical composition of sputter deposited nanostructured Cr-WS_2 solid lubricant coatings[J].Surface & Coatings Technology,20102(2):565-574. |
| [5] | 李斐;甄乾;张兴华;马吉强;徐建林;杨军.Fe3Al/WS2复合材料的真空摩擦学性能研究[J].摩擦学学报,2014(2):146-152. |
| [6] | 周磊;尹桂林;王玉东;余震;何丹农.反应溅射WS2/MoS2/C复合薄膜的摩擦磨损性能[J].中国有色金属学报,2010(3):483-487. |
| [7] | 章小峰;王爱华;张祥林;乔晓勇;黄早文.激光熔覆Ni45-CaF2-WS2自润滑涂层组织与性能[J].中国有色金属学报,2008(2):215-220. |
| [8] | 钱刚;凤仪;陈阳明;莫飞;王雨晴;刘文宏.二硫化钨含量对铜-石墨-二硫化钨复合材料电滑动磨损性能的影响[J].中国有色金属学报（英文版）,2015(6):1986-1994. |
| [9] | Watanabe S;Noshiro J;Miyake S.Friction properties of WS2/MoS2 multilayer films under vacuum environment[J].Surface & Coatings Technology,20040(0):644-648. |
| [10] | 解志文;王浪平;王小峰;黄磊;陆洋;闫久春.多元等离子体浸没离子注入与沉积和磁控溅射技术制备TiAlSiN/WS2多层薄膜的力学性能和腐蚀行为[J].中国有色金属学报（英文版）,2011(z2):470-475. |
| [11] | Chen, D.;Jiang, B.;Shi, H.;Long, Y..Effect of ion cleaning pretreatment on interface microstructure, adhesive strength and tribological properties of GLC coatings on Al substrates[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,201210(10):1576-1582. |
| [12] | 王佳凡;王永欣;陈克选;李金龙;郭峰.Cr掺杂对GLC薄膜结构及其摩擦学性能的影响[J].摩擦学学报,2015(2):206-213. |
| [13] | 权鑫;孙嘉奕;翁立军.WS2薄膜/空间液体润滑剂复合润滑体系的摩擦学性能研究[J].摩擦学学报,2014(6):665-672. |
| [14] | W. Lauwerens;Jihui Wang;J. Navratil;E. Wieers;J. D'haen;L. M. Stals;J. P. Celis;Y. Bruynseraede.Humidity resistant MoS{sub}x films prepared by pulsed magnetron sputtering[J].Surface & Coatings Technology,20001/3(1/3):216-221. |
| [15] | 王翔;代明江;戴达煌;侯惠君;林松盛.WC/DLC纳米多层膜微观结构研究[J].真空科学与技术学报,2013(1):41-44. |
| [16] | 李长生;于云;刘艳清;郝茂德;余应明.WS2纳米颗粒的合成及摩擦学性能研究[J].无机化学学报,2008(2):275-279. |
| [17] | Sanchez-Lopez JC;Martinez-Martinez D;Lopez-Cartes C;Fernandez A.Tribological behaviour of titanium carbide/amorphous carbon nanocomposite coatings: From macro to the micro-scale[J].Surface & Coatings Technology,200816(16):4011-4018. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%