用超声气体雾化法制备了一种快凝Ni-Mo-Cr-B合金微晶粉末,使用常规的等离子喷涂工艺可以将该粉末沉积在金属基体上形成一个致密的涂层。该涂层具有较高的结合强度和硬度,在不同的腐蚀介质中显示出较好的耐蚀性和耐磨性.经X射线衍射,差热分析和透射电镜做的微晶结构分析表明,快凝镍基微晶粉末经过等离子喷涂后发生了非晶转变,所获得的非晶涂层具有较高的热稳定性,在600℃以下的温度范围内不发生晶化过程,与此同时对比了同一种粉末采用氧乙炔火焰喷涂的不同工艺后涂层力学性能的差别。
Rapidly solidfied fine Ni-Mo-Cr-B alloy powders were prepared by ultrasonic gas atomization, which were subsequently applied to a metal subsrate by conventional plasma spraying. The coating showed high bond strength and hardness and exhibit good corrosion