采用熔体快淬法制备了成分为(Nd0.4Pr0.6),Fe76B15和(Nd0.4Pr0.6)9Fe72Ti4B15-yCy(y=0～4)的合金薄带,研究了Ti和C含量对快淬带非晶形成、晶化过程及磁性能的影响.结果表明:Ti和C的添加极大地促进了快淬带的非晶形成能力.随C含量增加,非晶形成能力增强,当y=4时,只需要7m/s辊速就可以得到完全非晶,最佳热处理后磁性能达到:Br=0.88T,Hci:618kA/m,(BH)max=109.8kJ/m3.研究还表明,添加Ti元素可以避免(Nd0.4Pr0.6)9Fe76B15,非晶晶化过程中(Nd,Pr):Fe23B3亚稳相和(Nd,Pr)1.1Fe4 B4相的生成,从而大大提高矫顽力.(Nd0.4Pr0.6)9Fe76B15,合金的晶化过程为:Amorphous phase(A)→(Nd,Pr):Fe23B3→(Nd,Pr)2Fe14B+α-Fe→(Nd,Pr)2 Fe14B+(Nd,Pr)1.1 Fe4 B4+α-Fe.而(Nd0.4Pr0.6)9Fe72Ti4B15合金的晶化过程为:Amorhous phase(A)→α-Fe+A'→(Nd,Pr)2Fe14B+α-Fe+Fe3B.
参考文献
| [1] | Kramer MJ.;Dennis KW.;McCallum RW.;Sellers CH.;Branagan DJ. Lewis LH.;Wang JY.;Li CP. .Effect of TiC additions to the microstructure and magnetic properties of Nd9.5Fe84.5B6 melt-spun ribbons[J].Journal of Applied Physics,1998(11 Pt.2):6631-6633. |
| [2] | 成份及组织结构对Pr2Fe14B/α-Fe纳米晶复合永磁材料晶粒间相互作用的影响[J].自然科学进展,2001(07):735-739. |
| [3] | Hirosawa S;Kaneklyo H;Miyoshi T .Unusual effects of Ti and C additions on structural and magnetic properties of Nd-Fe-B nanocomposite magnets in a B-rich and Nd-poor composition range[J].Journal of Magnetism and Magnetic Materials,2004(1):58-67. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%