Copper-manganese-aluminum (CMA) alloys, containing small additions of Fe, Ni, and Si, exhibit good strength and remarkable corrosion resistance against sea water. The alloys are used in as-cast condition, and their microstructure can show wide variations. The morphology, crystallography and composition of the phases presented in an as-cast (CMA) alloy of nominal composition Cu-14%Mn-8%Al-3%Fe-2%Ni were investigated using optical, electron optical, and microprobe analytical techniques. The as-cast microstructure consisted of the grains of fcc α and bcc β-phases alongwith intermetallic precipitates of various morphologies. The dendritic-shaped particles and the cuboid-shaped precipitates, which were rich in Fe and Mn and had an fcc DO3 structure. These four different morphologies of intermetallic precipitates exhibited discrete orientationrelationships with the α-matrix. The β-grains only contained very small cuboid shaped precipitates, which could only be resolved through transmission electron microscopy. These precipitates were found to be based on Fe3Al and had the DO3 structure.
参考文献
| [1] | P J Macken;A A Smith.The Aluminum Bronzes[M].CDA,London,1966:224. |
| [2] | F Hasan;A Jahanfrooz;G W Lorimer;N Ridley .[J].Metallurgical and Materials Transactions,1982,13A:1337. |
| [3] | F Hasan .[D].Univ of Manchester,1984. |
| [4] | J M Langam;A W O Webb .[J].Modern Casting,1962,42:62. |
| [5] | J O Edwards;D A Whittaker .[J].Transactions of AFS,1961,69:862. |
| [6] | K Rutkowski .[J].Modern Casting,1962,41:99. |
| [7] | N Bailey;A W O Webb .[J].Transactions of AFS,1964,72:321. |
| [8] | L Raymond .[J].Transactions of AFS,1979,87:537. |
| [9] | G Bradshaw;M M Kennedy;S H Dorn .[J].Modern Casting,1960,39:67. |
| [10] | J M Langham;A W O Webb .[J].British Foundrymen,1962,55:686. |
| [11] | P Brezina .[J].Institute Met Rev,1982,27:77. |
| [12] | J N Bradley .[J].Institute Met Rev,1972,17:88. |
| [13] | M Cook;W P Fentiman;E Davis .[J].Journal of the Institute of Metals,1952,80:419. |
| [14] | D R F West;D O L Thomas .[J].Journal of the Institute of Metals,1956,85(57):505. |
| [15] | O Knotek .[J].Tech Rundsch Bern,1968,60(16):25. |
| [16] | G Cliff;G W Lorimer .[J].Journal of Microscopy,1975,103:203. |
| [17] | J I Goldstein;J L Costley;G W Lorimer;S R J Reed.[A].Chicago:315. |
| [18] | J Iqbal;F Hasan.[A].Dhaka,2004:129. |
| [19] | F Hasan;G W Lorimer;N Ridley .[J].Journal of Phys Coloque C,1982,43:653. |
| [20] | M Bouchard;G Thomas .[J].ACTA METALLURGICA ET MATERIALIA,1975,23:1485. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%